Structure of nanoporous carbon materials for supercapacitors

Activated carbons with highly developed porous structure and nanosized pores (8 - 11 angstrom) were prepared from alder wood using thermochemical activation method with sodium hydroxide. Properties of the obtained activated carbons were examined by benzene and nitrogen sorption, X-Ray diffraction and Raman spectroscopy. Tests of activated carbons as electrodes in supercapacitors were performed as well. It was found that specific surface area of above mentioned activated carbons was 1800 m(2)/g (Dubinin - Radushkevich). Raman spectroscopy demonstrated the presence of ordered and disordered structures of graphite origin. The performance of activated carbons as electrodes in supercapacitors have shown superior results in comparison with electrodes made with commercial carbon tissues.