Effect of Thermal Aging on the Corrosion and Microstructure of Friction-Stir Welded Alloy 22

被引：1

作者：

Jasthi, Bharat K. ^{[1
,2
]}

Arbegast, William J. ^{[1
,3
]}

Howard, Stanley M. ^{[2
]}

机构：

[1] S Dakota Sch Mines & Technol, Adv Mat Proc AMP Ctr, Rapid City, SD 57701 USA

[2] S Dakota Sch Mines & Technol, Dept Mat & Met Engn, Rapid City, SD 57701 USA

[3] S Dakota Sch Mines & Technol, NSF Ctr Frict Stir Proc CFSP, Rapid City, SD 57701 USA

来源：

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 2012年 / 43A卷 / 09期

关键词：

STRAIN RATE SUPERPLASTICITY; GRAIN-SIZE; BEHAVIOR; SENSITIZATION; TEXTURE; FLOW;

D O I：

10.1007/s11661-012-1141-5

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The effect of thermal aging on the corrosion and microstructure of friction-stir welded (FSW) alloy 22 was investigated. Successful welds were produced with a polycrystalline cubic BN pin tool at a rotational speed of 200 rev min(-1) and travel speed of 12.7 mm min(-1). Topologically closed packed (TCP) phases of similar to 50 to 300 nm size were identified in the weld nugget. The area fraction of the TCP phases in the weld nugget increased with aging temperature and time. General corrosion rates measured from the weight loss experiments for welds were relatively higher than for parent material. The corrosion rates increased with the increased aging temperature and time. Intergranular corrosion (IGC) resistance is greater in friction-stir welds compared with the parent material at all aging temperatures and times. The IGC depth increased with the aging temperature and time in the parent material. The IGC depth for the FSW weld nugget was minimal and did not change with thermal aging.

引用

页码：3192 / 3201

页数：10

共 50 条

[41] Microstructure and pitting corrosion of friction Stir welded joints in 2219-O aluminum alloy thick plate
Xu, Weifeng
Liu, Jinhe
CORROSION SCIENCE, 2009, 51 (11) : 2743 - 2751
[42] Effect of ultrasonic vibration and heat pipe assistance on microstructure and mechanical properties of friction stir-welded AZ31 alloy
Zang, Qianhao
Yu, Jingmin
Peng, Jinhua
Chen, Liangyu
Wang, Zexin
Lu, Sheng
INTERNATIONAL JOURNAL OF MODERN PHYSICS B, 2022, 36 (12N13):
[43] Superplasticity of friction-stir welded Al-Mg-Sc sheets with ultrafine-grained microstructure
Malopheyev, S.
Mironov, S.
Vysotskiy, I.
Kaibyshev, R.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 649 : 85 - 92
[44] Corrosion susceptibility of peened friction stir welded 7075 aluminum alloy joints
Hatamleh, Omar
Singh, Preet M.
Garmestani, Hamid
CORROSION SCIENCE, 2009, 51 (01) : 135 - 143
[45] Microstructure and texture investigation on electrically assisted friction stir welded titanium alloy
Jiang, Xiaoqing
Han, Yang
Chen, Shujun
Bai, Yafeng
Yuan, Tao
Wang, Xuping
MATERIALS SCIENCE AND TECHNOLOGY, 2020, 36 (15) : 1628 - 1638
[46] Microstructure, texture, and mechanical properties of friction stir welded commercial brass alloy
Heidarzadeh, A.
Saeid, T.
Klemm, V.
MATERIALS CHARACTERIZATION, 2016, 119 : 84 - 91
[47] Material flow and microstructure evolution on the flow path of friction stir lap welded aluminium alloy
Han, Yang
Jiang, Xiaoqing
Yuan, Tao
Chen, Shujun
Gong, Wentao
Li, Xiaoxu
Yu, Zhanliang
SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2023, 28 (01) : 72 - 80
[48] Corrosion Analysis of Friction Stir-welded AA 7075 Aluminium Alloy
Elatharasan, Govindaraj
Kumar, Velukkudi Santhanam Senthil
STROJNISKI VESTNIK-JOURNAL OF MECHANICAL ENGINEERING, 2014, 60 (01): : 29 - 34
[49] Stress corrosion cracking of a friction stir welded precipitation hardening aluminum alloy
Cabrini, M.
Lorenzi, S.
Testa, C.
Galizzi, N.
Carugo, F.
Bocchi, S.
D'Urso, G.
Giardini, C.
Pastore, T.
METALLURGIA ITALIANA, 2021, 113 (03): : 6 - 14
[50] Incremental forming of friction-stir welded aluminium blanks: an integrated approach
Carlone, P.
Thuillier, S.
Andrade-Campos, A.
Alves de Sousa, R. J.
Valente, R.
INTERNATIONAL JOURNAL OF MATERIAL FORMING, 2021, 14 (05) : 1121 - 1137

← 1 2 3 4 5 →