Lap joining of TC4 titanium alloy to 304 stainless steel with fillet weld by GTAW using copper-based filler wire

被引：77
|
作者：
Hao, Xiaohu [1 ]
Dong, Honggang [1 ]
Li, Shuai [1 ]
Xu, Xinxing [1 ]
Li, Peng [1 ]
机构：
[1] Dalian Univ Technol, Sch Mat Sci & Engn, Dalian 116024, Peoples R China
来源：
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY | 2018年 / 257卷
基金：
中国国家自然科学基金; 中国博士后科学基金;
关键词：
Titanium alloy; Stainless steel; GTAW; Intermetallic compound; Microstructure; Mechanical property; DIFFUSION-BONDED JOINTS; STAINLESS-STEEL; INTERFACE MICROSTRUCTURE; STRENGTH PROPERTIES; MECHANICAL-PROPERTIES; HEAT-TREATMENT; ELECTRON-BEAM; 40CR STEEL; INTERLAYER; CU;
D O I：
10.1016/j.jmatprotec.2018.02.020
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
TiFe and TiFe2 intermetallic compounds (IMCs) were effectively suppressed with copper -based filler wire when joining TC4 titanium alloy to 304 stainless steel by gas tungsten arc welding (GTAW). A Ti/Cu reaction zone, consisting of various IMCs like Ti2Cu, A1Cu(2)Ti, TiCu, Ti3Cu4 phases, formed between TC4 substrate and the weld. Increasing welding heat input induced the formation of TiFe, TiFe2 and complex Ti Cu Al Fe IMCs in the Ti/Cu reaction zone. The highest shear fracture load occurred at welding heat input of 2.34 kJ/cm reached 341 N/mm corresponding to 107 MPa in shear strength, and the microhardness in the Ti/Cu reaction zone was about 619 HV. Further increasing welding heat input deteriorated the shear fracture load and increased the micro hardness in the Ti/Cu reaction zone. All joints fractured at the Ti/Cu reaction zone with cleavage characteristics on the fracture surface due to the brittle IMCs and micro cracks generated in the Ti/Cu reaction zone.
引用
收藏
页码：88 / 100
页数：13
相关论文
共 50 条
  • [31] Effect of Post-weld Heat Treatment on Properties of Friction Welded Joint Between TC4 Titanium Alloy and 40Cr Steel Rods
    Dong, Honggang
    Yu, Lianzhen
    Deng, Dewei
    Zhou, Wenlong
    Dong, Chuang
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2015, 31 (09) : 962 - 968
  • [32] Microstructure and Mechanical Property Improvement in Laser-Welded TC4 Titanium Alloy and 301L Stainless Steel Joints Without Filler Metal
    Zhang, Yan
    Sun, Da-Qian
    Gu, Xiao-Yan
    Li, Hong-Mei
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2019, 28 (01) : 140 - 153
  • [33] Microstructure and Mechanical Properties of Laser Welding Joints between TC4 Titanium Alloy and 304SS Stainless Steel Using Zr-Ni Multi-Interlayer
    Zhang Y.
    Zhang H.
    Su Z.
    Zhu Z.
    Pan J.
    Xiyou Jinshu/Chinese Journal of Rare Metals, 2020, 44 (11): : 1137 - 1145
  • [34] Laser-Arc Hybrid Welding of Dissimilar Titanium Alloy and Stainless Steel Using Copper Wire
    Gao, Ming
    Chen, Cong
    Wang, Lei
    Wang, Zemin
    Zeng, Xiaoyan
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2015, 46A (05): : 2007 - 2020
  • [35] Vacuum Brazing TC4 Titanium Alloy to 304 Stainless Steel with Cu-Ti-Ni-Zr-V Amorphous Alloy Foil
    Honggang Dong
    Zhonglin Yang
    Zengrui Wang
    Dewei Deng
    Chuang Dong
    Journal of Materials Engineering and Performance, 2014, 23 : 3770 - 3777
  • [36] Microstructure and mechanical properties of TC4/Q235 dual-beam laser lap joint using Cu-Si filler wire
    Zhang, Wendong
    Lang, Qiang
    Chen, Shuaishuai
    Shi, Shuyan
    Wang, Hongyang
    Liu, Liming
    OPTICS AND LASER TECHNOLOGY, 2024, 168
  • [37] Comparison of fatigue performance of TC4 titanium alloy welded by electron beam welding and laser welding with filler wire
    Long, Jian
    Zhang, Lin-Jie
    Zhang, Li-Xu
    Wu, Jun
    Zhuang, Ming-Xiang
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2022, 45 (04) : 991 - 1004
  • [38] Effect of welding heat input on microstructure and properties of TC4 titanium alloy ultra-narrow gap welded joint by laser welding with filler wire
    Fang, Naiwen
    Guo, Erjun
    Huang, Ruisheng
    Yin, Limeng
    Chen, Yongsheng
    Zeng, Caiyou
    Cao, Hao
    Zou, Jipeng
    Xu, Kaixin
    MATERIALS RESEARCH EXPRESS, 2021, 8 (01)
  • [39] Brazing process of TC4 titanium/ 304 stainless steel dissimilar materials honeycomb sandwich structure
    Deng Y.
    Yue X.
    Li X.
    Tao J.
    Zhang S.
    Hanjie Xuebao/Transactions of the China Welding Institution, 2019, 40 (10): : 148 - 155
  • [40] Microstructure and Mechanical Property Improvement of Dissimilar Metal Joints for TC4 Ti Alloy to 304 Stainless Steel Using TA2/Q235 Composite Interlayer
    Zhang, Yan
    Gao, YiDi
    Zhou, JianPing
    Sun, DaQian
    Li, HongMei
    METALS AND MATERIALS INTERNATIONAL, 2021, 27 (05) : 1224 - 1235
12345