Lap joining of TC4 titanium alloy to 304 stainless steel with fillet weld by GTAW using copper-based filler wire

被引：83

作者：

Hao, Xiaohu ^{[1
]}

Dong, Honggang ^{[1
]}

Li, Shuai ^{[1
]}

Xu, Xinxing ^{[1
]}

Li, Peng ^{[1
]}

机构：

[1] Dalian Univ Technol, Sch Mat Sci & Engn, Dalian 116024, Peoples R China

来源：

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY | 2018年 / 257卷

基金：

中国博士后科学基金; 中国国家自然科学基金;

关键词：

Titanium alloy; Stainless steel; GTAW; Intermetallic compound; Microstructure; Mechanical property; DIFFUSION-BONDED JOINTS; STAINLESS-STEEL; INTERFACE MICROSTRUCTURE; STRENGTH PROPERTIES; MECHANICAL-PROPERTIES; HEAT-TREATMENT; ELECTRON-BEAM; 40CR STEEL; INTERLAYER; CU;

D O I：

10.1016/j.jmatprotec.2018.02.020

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

TiFe and TiFe2 intermetallic compounds (IMCs) were effectively suppressed with copper -based filler wire when joining TC4 titanium alloy to 304 stainless steel by gas tungsten arc welding (GTAW). A Ti/Cu reaction zone, consisting of various IMCs like Ti2Cu, A1Cu(2)Ti, TiCu, Ti3Cu4 phases, formed between TC4 substrate and the weld. Increasing welding heat input induced the formation of TiFe, TiFe2 and complex Ti Cu Al Fe IMCs in the Ti/Cu reaction zone. The highest shear fracture load occurred at welding heat input of 2.34 kJ/cm reached 341 N/mm corresponding to 107 MPa in shear strength, and the microhardness in the Ti/Cu reaction zone was about 619 HV. Further increasing welding heat input deteriorated the shear fracture load and increased the micro hardness in the Ti/Cu reaction zone. All joints fractured at the Ti/Cu reaction zone with cleavage characteristics on the fracture surface due to the brittle IMCs and micro cracks generated in the Ti/Cu reaction zone.

引用

页码：88 / 100

页数：13

共 29 条

[1] Experimental study of diffusion welding/bonding of titanium to copper [J].

Aydin, Kemal ;

Kaya, Yakup ;

Kahraman, Nizamettin .

MATERIALS & DESIGN, 2012, 37 :356-368

[2]

Baker H., 1992, ASM HDB ALLOY PHASE, V3

[3] Study on cold metal transfer welding-brazing of titanium to copper [J].

Cao, R. ;

Feng, Z. ;

Lin, Q. ;

Chen, J. H. .

MATERIALS & DESIGN, 2014, 56 :165-173

[4] Microstructures and mechanical property of laser butt welding of titanium alloy to stainless steel [J].

Chen, Shuhai ;

Zhang, Mingxin ;

Huang, Jihua ;

Cui, Chengji ;

Zhang, Hua ;

Zhao, Xingke .

MATERIALS & DESIGN, 2014, 53 :504-511

[5] FEM prediction of welding residual stresses in a SUS304 girth-welded pipe with emphasis on stress distribution near weld start/end location [J].

Deng, Dean ;

Kiyoshima, Shoichi .

COMPUTATIONAL MATERIALS SCIENCE, 2010, 50 (02) :612-621

[6] Joining of titanium to 304L stainless steel by friction welding [J].

Dey, H. C. ;

Ashfaq, M. ;

Bhaduri, A. K. ;

Rao, K. Prasad .

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2009, 209 (18-19) :5862-5870

[7] Effect of Post-weld Heat Treatment on Properties of Friction Welded Joint Between TC4 Titanium Alloy and 40Cr Steel Rods [J].

Dong, Honggang ;

Yu, Lianzhen ;

Deng, Dewei ;

Zhou, Wenlong ;

Dong, Chuang .

JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2015, 31 (09) :962-968

[8] CuTiNiZrV Amorphous Alloy Foils for Vacuum Brazing of TiAl Alloy to 40Cr Steel [J].

Dong, Honggang ;

Yang, Zhonglin ;

Wang, Zengrui ;

Deng, Dewei ;

Dong, Chuang .

JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2015, 31 (02) :217-222

[9] Vacuum brazing of TiAl alloy to 40Cr steel with Ti60Ni22Cu10Zr8 alloy foil as filler metal [J].

Dong, Honggang ;

Yang, Zhonglin ;

Yang, Guoshun ;

Dong, Chuang .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2013, 561 :252-258

[10] Improving arc joining of Al to steel and Al to stainless steel [J].

Dong, Honggang ;

Yang, Liqun ;

Dong, Chuang ;

Kou, Sindo .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2012, 534 :424-435

← 1 2 3 →