On a determination of wear resistance and adhesion of molybdenum, Cr-Ni and Cr-Mn steel coatings thermally sprayed on a 35CrMo4 steel

被引:11
作者
Laribi, M
Vannes, AB
Treheux, D
机构
[1] Ecole Natl Polytech Alger, Dept Met, Algiers, Algeria
[2] Ecole Cent Lyon, CNRS, Dept STMS, UMR 5621, F-69134 Lyon, France
关键词
molybdenum; Cr-Ni and Cr-Mn steels; coatings; thermal spraying; 35CrMo4; substrate; post annealing; HV microhardness; adhesion; wear resistance; oil lubrication;
D O I
10.1016/j.surfcoat.2004.12.036
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
This paper aims to show the relationship between, on one hand, the deposition and post-deposition conditions, and on the other hand, the adherence and wear resistance of molybdenum and Cr-Ni-Mn alloyed steel coatings thermally sprayed on a 35CrMo4 steel substrate. The adherence to steel substrate was determined using a four-point "delamination" test bend and the tribological behavior of coatings has been studied using a simple ball-on-plate tribometer. The study has also been focused on the influence of a post-annealing at 850 degrees C for 1h in vacuum followed by air cooling on the adherence of the two different coatings on the steel substrate and on their wear resistance under specific wear and lubrication conditions. Flame sprayed molybdenum showed high tribological behavior and strong adhesion in relation with its metallurgical nature and the substrate surface preparation. Post annealing and lubrication are rather beneficial for electric arc sprayed steel coating. The first one improved its adhesion to substrate and the second decreased its friction coefficient against a hardened 100Cr6 steel ball. (c) 2005 Elsevier B.V All rights reserved.
引用
收藏
页码:2704 / 2710
页数:7
相关论文
共 15 条
  • [1] A test specimen for determining the fracture resistarim of bimaterial interfaces
    Charalambides, PG
    Lund, J
    Evans, AG
    McMeeking, RM
    [J]. JOURNAL OF APPLIED MECHANICS-TRANSACTIONS OF THE ASME, 1989, 56 (01): : 77 - 82
  • [2] GUIPONT V, 1994, THESIS E C LYON FRAN
  • [3] Hansen M., 1958, METALLURGY METALLURG
  • [4] Herman H., 2000, MRS B, V25
  • [5] CHARACTERIZATION OF FLAME-SPRAYED AND PLASMA-SPRAYED PURE METALLIC AND ALLOYED COATINGS
    IORDANOVA, I
    FORCEY, KS
    GERGOV, B
    BOJINOV, V
    [J]. SURFACE & COATINGS TECHNOLOGY, 1995, 72 (1-2) : 23 - 29
  • [6] Texture and residual stresses in thermally sprayed coatings
    Iordanova, I
    Forcey, KS
    [J]. SURFACE & COATINGS TECHNOLOGY, 1997, 91 (03) : 174 - 182
  • [7] LALLEMANDTALLAR.G, 1996, THESIS E C LYON FRAN
  • [8] Metallurgical characterization and determination of residual stresses of coatings formed by thermal spraying
    Laribi, M
    Vannes, AB
    Mesrati, N
    Treheux, D
    [J]. JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2003, 12 (02) : 234 - 239
  • [9] Adhesion and residual stresses determination of thermally sprayed molybdenum on steel
    Laribi, M
    Mesrati, N
    Vannes, AB
    Treheux, D
    [J]. SURFACE & COATINGS TECHNOLOGY, 2003, 166 (2-3) : 206 - 212
  • [10] LARIBI M, 2001, MAT TECH J, V9, P15