Subcritical crack growth in Low Temperature Co-fired Ceramics under biaxial loading

被引：32

作者：

Bermejo, R. ^{[1
]}

Supancic, P. ^{[1
,2
]}

Krautgasser, C. ^{[2
]}

Morrell, R. ^{[1
,3
]}

Danzer, R. ^{[1
,2
]}

机构：

[1] Univ Leoben, Inst Struktur & Funkt Keram, A-8700 Leoben, Austria

[2] Mat Ctr Leoben, A-8700 Leoben, Austria

[3] Natl Phys Lab, Teddington TW11 0LW, Middx, England

来源：

ENGINEERING FRACTURE MECHANICS | 2013年 / 100卷

关键词：

Low Temperature Co-fired Ceramics; Environmentally assisted cracking; Fracture mechanics; Failure assessment; Lifetime prediction; 3 BALLS TEST; LIFETIME MEASUREMENTS; BRITTLE DISCS; STRENGTH; PROPAGATION; FRACTURE; WATER; TOUGHNESS; FLEXURE; GLASS;

D O I：

10.1016/j.engfracmech.2012.12.004

中图分类号：

O3 [力学];

学科分类号：

08 ; 0801 ;

摘要：

The biaxial strength of Low Temperature Co-fired Ceramics was determined using the ballon-three-balls test in several environments (dry oil, air and water). Subcritical crack growth phenomenon was observed, activated by the prolonged presence of humidity at the specimen surface. Whereas high strength values were reached during high-rate testing in dry oil, up to a 50% lower strength was measured on specimens immersed in water tested for longer periods. Experiments in a relative dry environment have shown for the first time evidence of two different crack growth mechanisms in this material. A model has been implemented to interpret the experimental results. (C) 2012 Elsevier Ltd. All rights reserved.

引用

页码：108 / 121

页数：14

共 46 条

[11] The ball on three balls test for strength testing of brittle discs:: stress distribution in the disc
Börger, A
Supancic, P
Danzer, R
[J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2002, 22 (9-10) : 1425 - 1436
[12] DYNAMIC FATIGUE OF GLASS
CHARLES, RJ
[J]. JOURNAL OF APPLIED PHYSICS, 1958, 29 (12) : 1657 - 1662
[13] Critical notch-root radius effect in SENB-S fracture toughness testing
Damani, R
Gstrein, R
Danzer, R
[J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 1996, 16 (07) : 695 - 702
[14] Lifetime prediction for mechanically stressed low temperature co-fired ceramics
Dannheim, H
Schmid, U
Roosen, A
[J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2004, 24 (08) : 2187 - 2192
[15] DANZER R, 1993, ENCY MAT SCI ENG, P1557
[16] Fracture of ceramics
Danzer, Robert
Lube, Tanja
Supancic, Peter
Damani, Rajiv
[J]. ADVANCED ENGINEERING MATERIALS, 2008, 10 (04) : 275 - 298
[17] The ball on three balls test -: Strength and failure analysis of different materials
Danzer, Robert
Harrer, Walter
Supancic, Peter
Lube, Tanja
Wang, Zhonghua
Boerger, Andreas
[J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2007, 27 (2-3) : 1481 - 1485
[18] Biaxial tensile strength test for brittle rectangular plates
Danzer, Robert
Supancic, Peter
Harrer, Walter
[J]. JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 2006, 114 (1335) : 1054 - 1060
[19] Davidge R., 1979, MECH BEHAV CERAMICS
[20] PROOF TESTING OF CERAMIC MATERIALS - ANALYTICAL BASIS FOR FAILURE PREDICTION
EVANS, AG
WIEDERHORN, SM
[J]. INTERNATIONAL JOURNAL OF FRACTURE, 1974, 10 (03) : 379 - 392

← 1 2 3 4 5 →