A TiCx reinforced Fe (Al) matrix composite using in-situ reaction

被引：28

作者：

Chen, Xinhua ^{[1
]}

Zhai, Hongxiang ^{[1
]}

Wang, Wenjuan ^{[1
]}

Li, Shibo ^{[1
]}

Huang, Zhenying ^{[1
]}

机构：

[1] Beijing Jiaotong Univ, Inst Mat Sci & Engn, Beijing 100044, Peoples R China

来源：

PROGRESS IN NATURAL SCIENCE-MATERIALS INTERNATIONAL | 2013年 / 23卷 / 01期

关键词：

Fe matrix composite; TiCx grain reinforcement; Ti3AlC2 Phase transformation; Tensile behavior; TI3ALC2; MICROSTRUCTURE; CU; NANOCOMPOSITES; CU-TI3ALC2; ALUMINUM; CERMET; ALLOY;

D O I：

10.1016/j.pnsc.2013.01.002

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

A new Fe matrix composite reinforced by the in-situ generated TiCx grains was prepared using the element Fe and Ti3AlC2 powders as the starting materials. Several hot-pressing temperatures were tried for exploring the phase transformation behavior from Ti3AlC2 to TiCx. Microstructures of the hot-pressed product were observed and analyzed. A tensile test was carried out for the new composite material, and the fracture face was analyzed. The results showed that the starting Ti3AlC2 was wholly decomposed and transformed into submicron TiCx grains at the hotpressing temperature above 1100 degrees C. Most of the Al ions escaped from Ti3AlC2 were aggregated at the grain boundary of Fe grains, but a small amount of Al ions could be absorbed by Fe and formed Fe(Al) alloy around the surface of Fe grains. The prepared material exhibited a higher tensile strength of about 660 MPa and a uniform deformation of about 7%. (C) 2013 Chinese Materials Research Society. Production and hosting by Elsevier B.V. All rights reserved.

引用

页码：13 / 17

页数：5

共 40 条

[1] Interformational exfoliation of Ti3AlC2 induced by Cu [J].

Ai, Mingxing ;

Zhai, Hongxiang ;

Tang, Zhaoyun .

HIGH-PERFORMANCE CERAMICS IV, PTS 1-3, 2007, 336-338 :1371-1373

[2]

Ai MX, 2006, J AM CERAM SOC, V89, P1114, DOI [10.1111/j.1551-29162005.00818.x, 10.1111/j.1551-2916.2005.00818.x]

[3]

[Anonymous], 2003, Nanocomposite science and technology

[4] The MN+1AXN phases:: A new class of solids;: Thermodynamically stable nanolaminates [J].

Barsoum, MW .

PROGRESS IN SOLID STATE CHEMISTRY, 2000, 28 (1-4) :201-281

[5] Synthesis, Characterization, and Intrinsic Hardness of Layered Nanolaminate Ti3AlC2 and Ti3Al0.8Sn0.2C2 Solid Solution [J].

Bei, G. P. ;

Gauthier-Brunet, V. ;

Tromas, C. ;

Dubois, S. .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2012, 95 (01) :102-107

[6] Interface structure and radiation damage resistance in Cu-Nb multilayer nanocomposites [J].

Demkowicz, M. J. ;

Hoagland, R. G. ;

Hirth, J. P. .

PHYSICAL REVIEW LETTERS, 2008, 100 (13)

[7]

EREMENKO VN, 1963, ROLE SURFACE PHENOME

[8] THE YOUNG MODULI OF IN-SITU TI/TIB COMPOSITES OBTAINED BY RAPID SOLIDIFICATION PROCESSING [J].

FAN, Z ;

MIODOWNIK, AP ;

CHANDRASEKARAN, L ;

WARDCLOSE, M .

JOURNAL OF MATERIALS SCIENCE, 1994, 29 (04) :1127-1134

[9] Synthesis of carbide-free, high strength iron-carbon nanotube composite by in situ nanotube growth [J].

Goyal, Amit ;

Wiegand, Donald A. ;

Owens, Frank J. ;

Iqbal, Zafar .

CHEMICAL PHYSICS LETTERS, 2007, 442 (4-6) :365-371

[10]

Huang Z.Y., 2010, PREPARATION PROPERTI, P79

← 1 2 3 4 →