Analysis of temperature and fracture surface of AISI4140 steel in very high cycle fatigue regime

被引：31

作者：

Crupi, V. ^{[1
]}

Epasto, G. ^{[1
]}

Guglielmino, E. ^{[1
]}

Risitano, G. ^{[1
]}

机构：

[1] Univ Messina, Dept Elect Engn Chem & Ind Engn DIECII, I-98100 Messina, Italy

来源：

THEORETICAL AND APPLIED FRACTURE MECHANICS | 2015年 / 80卷

关键词：

Very high cycle fatigue; Gygacycles; Thermographic method; Thermography; Fracture surface analysis; ULTRASONIC FATIGUE; CRACK INITIATION; STRENGTH; BEHAVIOR; LIFE; FAILURE; LIMIT;

D O I：

10.1016/j.tafmec.2015.07.007

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

Currently, the technological progress in the engineering fields requires that the design lifetime of many components exceeds 107 loading cycles. The ultrasonic testing machines allow loading the specimen with 20 kHz frequency, allowing reaching gigacycles within a relatively short time, but the high value of frequency produce a high heating of the specimen. A controversy is still opened in literature about the effect of the temperature increase on the fatigue response. This aspect was investigated in the present study. Very high cycle fatigue tests were carried out on AISI4140 steel at frequency f = 20 kHz and stress ratio R = -1 with and without cooling the specimen during the test. The temperature evolution was detected during the whole fatigue test by means of an infrared camera. The fracture mechanism of the investigated steels was evaluated by means of several experimental techniques (Thermography and Optical Microscopy). (C) 2015 Elsevier Ltd. All rights reserved.

引用

页码：22 / 30

页数：9

共 31 条

[1] Rapid determination of fatigue failure based on temperature evolution: Fully reversed bending load [J].

Amiri, M. ;

Khonsari, M. M. .

INTERNATIONAL JOURNAL OF FATIGUE, 2010, 32 (02) :382-389

[2] Fatigue failure predictions for steels in the very high cycle region - A review and recommendations [J].

Bandara, Chaminda S. ;

Siriwardane, Sudath C. ;

Dissanayake, Udaya I. ;

Dissanayake, Ranjith .

ENGINEERING FAILURE ANALYSIS, 2014, 45 :421-435

[3]

Bathias C, 1999, FATIGUE FRACT ENG M, V22, P559, DOI 10.1046/j.1460-2695.1999.00183.x

[4]

Bathias C., 2005, MECH ENG SE

[5] Coupling effect of plasticity, thermal dissipation and metallurgical stability in ultrasonic fatigue [J].

Bathias, Claude .

INTERNATIONAL JOURNAL OF FATIGUE, 2014, 60 :18-22

[6]

BOKUVKA O, 2000, LOW HIGH FREQUENCY F

[7] A first approach to the analysis of fatigue parameters by thermal variations in static tests on plastics [J].

Clienti, C. ;

Fargione, G. ;

La Rosa, G. ;

Risitano, A. ;

Risitano, G. .

ENGINEERING FRACTURE MECHANICS, 2010, 77 (11) :2158-2167

[8] Experimental and numerical analysis of fillet-welded joints under low-cycle fatigue loading by means of full-field techniques [J].

Corigliano, Pasqualino ;

Crupi, Vincenzo ;

Fricke, Wolfgang ;

Friedrich, Nils ;

Guglielmino, Eugenio .

PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART C-JOURNAL OF MECHANICAL ENGINEERING SCIENCE, 2015, 229 (07) :1327-1338

[9] Thermographic method for very high cycle fatigue design in transportation engineering [J].

Crupi, V. ;

Epasto, G. ;

Guglielmino, E. ;

Risitano, G. .

PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART C-JOURNAL OF MECHANICAL ENGINEERING SCIENCE, 2015, 229 (07) :1260-1270

[10] Low-velocity impact strength of sandwich materials [J].

Crupi, V. ;

Epasto, G. ;

Guglielmino, E. .

JOURNAL OF SANDWICH STRUCTURES & MATERIALS, 2011, 13 (04) :409-426

← 1 2 3 4 →