Influence of Zinc on the Microstructure and Brittle Phases of Friction Stir Welded Joint of Al/Ti Dissimilar Alloys

被引：9

作者：

Chen, Yuhua ^{[1
]}

Yu, Liang ^{[1
]}

Ni, Quan ^{[1
]}

机构：

[1] Nanchang Hangkong Univ, Natl Def Key Disciplines Lab Light Alloy Proc Sci, Nanchang 330063, Peoples R China

来源：

MATERIALS SCIENCE AND ENGINEERING APPLICATION II | 2012年 / 413卷

关键词：

Ti/Al dissimilar alloys; Zinc; Friction stir welding; Microstructure; Brittle phases;

D O I：

10.4028/www.scientific.net/AMR.413.439

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Titanium alloy TC1 and Aluminum alloy LF6 were butt jointed by friction stir welding (FSW) using zinc as the middle layer material. Influence of zinc on the microstructure and brittle phases were studied. The results show that, the microstructure of the nuclear zone is a mixture structure with Ti alloy particles distributed on Al alloy substrate. At the same time, XRD test results show that there TiAl3 intermetallic compounds and Zn0.69Ti0.31 intermetallic compounds in the nuclear region. The joint which is added zinc as the middle layer material becomes more brittle.

引用

页码：439 / 443

页数：5

共 6 条

[1]

Chen Y. H., 2010, CHINESE J NONFERROUS, V20, P211

[2] Friction stir welding of titanium alloy TiAl6V4 to aluminium alloy AA2024-T3 [J].

Dressler, Ulrike ;

Biallas, Gerhard ;

Mercado, Ulises Alfaro .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2009, 526 (1-2) :113-117

[3]

Li Yajiang, 2007, MAT SCI TECHNOLOGY, V2, P206

[4]

Ni Jiaming, 2007, CHINESE J NONFERROUS, V4, P617

[5]

Qu Wenqing, 2002, ACTA METALLURGICA SI, V38, P311

[6]

Zhao PF, 2001, J MAT ENG, V4, P25

← 1 →