Effect of initial treatment on the structure and mechanical properties of medium carbon steel subjected to ECAP

被引:1
作者
Zrnik, J. [1 ]
Dobatkin, S. V. [2 ]
Raab, G. I. [3 ]
Kraus, L. [1 ]
机构
[1] COMTES FHT Inc, Dobrany 33441, Czech Republic
[2] RAS, Baikov Inst Met & Mat Sci, Moscow 117901, Russia
[3] Inst Phys Adv Mat, Ufa, Russia
来源
KOVOVE MATERIALY-METALLIC MATERIALS | 2013年 / 51卷 / 06期
关键词
carbon steel; microstructure; dissolving; TM treatment; SPD; ECAP; mechanical properties;
D O I
10.4149/km_2013_6_343
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The present work deals with grain refinement of medium carbon steel AISI 1045 (0.45 wt.% C) having different initial ferrite-pearlite microstructure resulted from thermal and thermomechanical (TM) treatment. The purpose of prior TM steel processing was to refine grains of ferrite phase and to modify coarse lamellae pearlite structure. The final grain refinement of steel structure was then accomplished during warm Equal Channel Angular Pressing (ECAP) deformation at 400 C. Employment of this processing route, in dependence of the applied effective strain epsilon(ef), resulted in extensive deformation of ferrite grains and cementite lamellae fragmentation. When applying higher shear stress, the mixed structure of subgrains and ultrafine grains was formed within ferrite phase, regardless the initial steel modification. In pearlite grains modification of cementite lamellae due to shearing, bending, twisting and breaking was found efficient as straining increased. Processes of dynamic polygonization and recrystallization in deformed structure also contributed to submicrocrystalline grains structure formation in intensively deformed structure. Comparing results of coarse lamellae cementite spheroidization it was then more efficient when prior TM treatment of steel was introduced. The tensile deformation results confirmed the strength increase, however, deformation behaviour and strain hardening, generally for different initial structural conditions of steel, showed diversity across deformed bars.
引用
收藏
页码:343 / 350
页数:8
相关论文
共 15 条
[1]   The evolution of ultrafine ferrite formation through dynamic strain-induced transformation [J].
Beladi, H ;
Kelly, GL ;
Shokouhi, A ;
Hodgson, PD .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 371 (1-2) :343-352
[2]  
Dobatkin S. V., 2000, INVESTIGATION APPL S
[3]   Processing of a low-carbon steel by equal-channel angular pressing [J].
Fukuda, Y ;
Oh-ishi, K ;
Horita, Z ;
Langdon, TG .
ACTA MATERIALIA, 2002, 50 (06) :1359-1368
[4]   Microstructure and microtexture of ultrafine ferrite formed in 0•1%C steel using new strip rolling process [J].
Hurley, PJ ;
Muddle, BC ;
Hodgson, PD .
MATERIALS SCIENCE AND TECHNOLOGY, 2000, 16 (11-12) :1376-1379
[5]  
PARK K. T., 2001, METALL MATER TRANS A, V32, P589
[6]  
Sastry S. M., 2004, METALS, V2, P129
[7]   MATERIALS PROCESSING BY SIMPLE SHEAR [J].
SEGAL, VM .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1995, 197 (02) :157-164
[8]  
SEGAL VM, 1981, RUSS METALL+, P99
[9]  
SEGAL VM, 1994, PROCESS PLASTIC STRU
[10]  
Shin D. H., 2011, ACTA MAT, V51, P983