Surface modification of PEEK by UV irradiation for direct co-curing with carbon fibre reinforced epoxy prepregs

被引：56

作者：

Shi, Huajie ^{[1
,2
]}

Sinke, Jos ^{[2
]}

Benedictus, Rinze ^{[2
]}

机构：

[1] Mat Innovat Inst M2i, Elektronicaweg 25, NL-2628 XG Delft, Netherlands

[2] Delft Univ Technol, Fac Aerosp Engn, Struct Integr & Composites Grp, Kluyverweg I, NL-2629 HS Delft, Netherlands

来源：

INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES | 2017年 / 73卷

关键词：

Composites; Thermoplastic; Surface treatment; Hybrid joints; INTERLAMINAR FRACTURE-TOUGHNESS; COMPOSITE-MATERIALS; BEHAVIOR;

D O I：

10.1016/j.ijadhadh.2016.07.017

中图分类号：

TQ [化学工业];

学科分类号：

0817 ;

摘要：

Adding a layer of thermoplastic resin on the surface of thermoset composites enables welding as a possible joining method for thermoset composites. Adhesion at the thermoset/thermoplastic interface was achieved by direct co-curing of an UV irradiation treated PEEK film with aerospace grade carbon/epoxy prepregs. The effectiveness of UV irradiation for surface modification of PEEK was characterized Using Fourier-Transformed InfraRed (FTIR) spectroscopy and contact angle measurement. The adhesion quality at the thermoset/thermoplastic interface was evaluated using a double cantilever beam test and Atomic Force Microscopy (AFM). UV treatment was found to effectively modify the chemical structure of PEEK surface and improve the wettability, which enables the development of a thermoset/thermoplastic interface by direct co-curing.

引用

页码：51 / 57

页数：7

共 28 条

[1] Resistance welding of thermosetting composite/thermoplastic composite joints [J].

Ageorges, C ;

Ye, L .

COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2001, 32 (11) :1603-1612

[2]

[Anonymous], 2001, ISO B 15024

[3] Morphology and fracture behavior of POM modified epoxy matrices and their carbon fiber composites [J].

Aravand, Mohammadali ;

Lomov, Stepan V. ;

Gorbatikh, Larissa .

COMPOSITES SCIENCE AND TECHNOLOGY, 2015, 110 :8-16

[4] Thermal degradation analysis of short-time heated polymers [J].

Bayerl, Thomas ;

Brzeski, Markus ;

Martinez-Tafalla, Manuel ;

Schledjewski, Ralf ;

Mitschang, Peter .

JOURNAL OF THERMOPLASTIC COMPOSITE MATERIALS, 2015, 28 (03) :390-414

[5]

Cole KC, POLYMER

[6]

Cole KC, THERMOCHIM ACTA

[7]

Deterts A, 2012, P 1 INT C EXH THERM

[8] Characterisation of interphase nanoscale property variations in glass fibre reinforced polypropylene and epoxy resin composites [J].

Gao, SL ;

Mäder, E .

COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2002, 33 (04) :559-576

[9] Photochemical evolution of poly(ether ether ketone) [J].

Giancaterina, S ;

Rossi, A ;

Rivaton, A ;

Gardette, JL .

POLYMER DEGRADATION AND STABILITY, 2000, 68 (01) :133-144

[10]

Hou M, 2011, P 7 INT C PROC MAN A, P2968

← 1 2 3 →