Controlling organization of conjugated polymer films from binary solvent mixtures for high performance organic field-effect transistors

We investigate the effect of a binary solvent blend as a solvent for poly{[N, N'-bis(2-octyldodecyl)-1,4,5,8-naphthalenediimide-2,6-diyl]-alt-5,5'-(2,2'-bithiophene)} P(NDI2OD-T2) on the characteristics of nchannel organic field-effect transistors (OFETs). To make the binary solvent blend, the low-boiling-point non-solvent propylene glycol methyl ether acetate (PGMEA, b.p similar to 146 degrees C) is added to the high-boiling-point good solvent 1,2-dichlorobenzene (O-DCB, b.p similar to 180 degrees C) at various mixing ratio from 0 to 40 v%. UV-vis spectra of P(NDI2OD-T2) solution dissolved in the binary solvent clearly show the formation of polymer aggregates through a gradual red shift of the intramolecular charge transfer band with the addition of high concentrations of non-solvent PGMEA. Higher edge-on oriented crystallinity is observed for P(NDI2OD-T2) films spin-coated from the binary solvent with 5-10 v% PGMEA by out-of-order x-ray diffraction. P(NDI2OD-T2) films are applied as the active layer in top-gate/bottom-contact OFETs. Improved n-type field-effect mobility of the P(NDI2OD-T2) semiconducting layer up to 0.59 cm(2)/Vs was achieved for on-center spin coated films compared to 1.03 cm(2)/Vs for off-center (parallel alignment) spin-coated films respectively employing the binary solvent with 10 v% PGMEA. (C) 2016 Elsevier B.V. All rights reserved.