Effect of Eu addition on the microstructures and mechanical properties of A356 aluminum alloys

被引:108
作者
Mao, Feng [1 ]
Yan, Guangyuan [1 ]
Xuan, Zhenjing [1 ]
Cao, Zhiqiang [2 ]
Wang, Tongmin [1 ]
机构
[1] Dalian Univ Technol, Sch Mat Sci & Engn, Key Lab Mat Modificat Laser Ion & Electron Beams, Minist Educ, Dalian 116024, Peoples R China
[2] Dalian Univ Technol, Lab Special Proc Raw Mat, Dalian 116024, Peoples R China
基金
中国国家自然科学基金;
关键词
Eutectic silicon; Eu modification; A356; Mechanical properties; AL-SI ALLOYS; EUTECTIC SI; TENSILE PROPERTIES; HEAT-TREATMENT; NUCLEATION; STRONTIUM; REFINEMENT; STRENGTH;
D O I
10.1016/j.jallcom.2015.06.266
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
The effect of Eu additions (0, 0.02, 0.04, 0.06, 0.08 and 0.1 wt.%) and T6 heat treatment on the microstructures and mechanical properties of A356 alloy have been investigated in the present work. Microstructures of the as-cast and T6 heat treated samples were examined by optical microscopy (OM) and scanning electron microscopy (SEM). It was found that 0.1% Eu modified the eutectic Si from a coarse plate-like form to a fully modified and fine fibrous one with a better uniform distribution. T6 treatment encouraged the spheroidization of eutectic Si particles. Correlating with the as-cast samples, the 0.1% Eu modified A356 alloy achieved likewise full modification of eutectic Si particles with lowest mean area and aspect ratio. In addition, the coarse and small Eu-rich intermetallics were both found in the 0.1% Eu modified A356 alloy. The cooling curves of A356 alloys showed that increasing Eu addition resulted in increasing nucleation undercooling and increasing growth undercooling. However, the recalescence (T-G - T-Min) increased by the initial addition of Eu, while it remained relatively stable for increasing additions (above 0.06%). The quenching experiment indicated that a large number of eutectic grains were located at or close to the tips of the aluminum dendrites with a jagged solid-liquid interface in unmodified alloy, while very few eutectic grains were formed in the interdendritic region with a smooth solid-liquid interface in 0.1% Eu modified alloy. An optimal combination of UTS (265 MPa) and EI (14.7%) of A356 alloy was achieved by the 0.1% Eu addition combined with T6 heat treatment. (C) 2015 Elsevier B.V. All rights reserved.
引用
收藏
页码:896 / 906
页数:11
相关论文
共 39 条
[1]  
Campbell J, 2011, COMPLETE CASTING HANDBOOK: METAL CASTING PROCESSES, METALLURGY, TECHNIQUES AND DESIGN, VOL 1 AND 2, P1
[2]   Effect of strontium and phosphorus on eutectic Al-Si nucleation and formation of β-Al5FeSi in hypoeutectic Al-Si foundry alloys [J].
Cho, Y. H. ;
Lee, H. -C. ;
Oh, K. H. ;
Dahle, A. K. .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2008, 39A (10) :2435-2448
[3]  
Crosley P.B., 1966, AFS T, V74, P53
[4]  
DROUZY M, 1980, INT CAST MET J, V5, P43
[5]   Evaluations of antimony and strontium interaction in an Al-Si-Cu-Zn die cast alloy [J].
Farahany, Saeed ;
Idris, Mohd Hasbullah ;
Ourdjini, Ali .
THERMOCHIMICA ACTA, 2014, 584 :72-78
[6]   Distribution of trace elements in a modified and grain refined aluminium-silicon hypoeutectic alloy [J].
Faraji, M. ;
Katgerman, L. .
MICRON, 2010, 41 (06) :554-559
[7]  
Gu G.D., 1990, FOUNDRY, V10, P32
[8]   HETEROGENEOUS NUCLEATION OF SOLIDIFICATION OF SI IN AL-SI AND AL-SI-P ALLOYS [J].
HO, CR ;
CANTOR, B .
ACTA METALLURGICA ET MATERIALIA, 1995, 43 (08) :3231-3246
[9]   MODIFICATION OF HYPOEUTECTIC AL-SI ALLOYS [J].
HO, CR ;
CANTOR, B .
JOURNAL OF MATERIALS SCIENCE, 1995, 30 (08) :1912-1920
[10]   Refinement of eutectic silicon phase of aluminum A356 alloy using high-intensity ultrasonic vibration [J].
Jian, X ;
Meek, TT ;
Han, Q .
SCRIPTA MATERIALIA, 2006, 54 (05) :893-896