Analysis of temperature distribution in the hot plate rolling of Mg alloy by experiment and finite element method

被引：41

作者：

Ding, Yunpeng ^{[1
]}

Zhu, Qiang ^{[1
]}

Le, Qichi ^{[1
]}

Zhang, Zhigiang ^{[1
]}

Bao, Lei ^{[1
]}

Cui, Jianzhong ^{[1
]}

机构：

[1] Northeastern Univ, Key Lab Electromagnet Proc Mat, Shenyang 110004, Peoples R China

来源：

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY | 2015年 / 225卷

关键词：

Magnesium alloy; Rolling; Finite element method; Temperature distribution; Heat transfer; AZ31 MAGNESIUM ALLOY; HEAT-TRANSFER; DEFORMATION; STATE; STRIP; RISE;

D O I：

10.1016/j.jmatprotec.2015.06.011

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The temperature distribution of Mg-3Al-Zn plate along the thickness and its variation history during rolling was measured by thermocouples embedded in samples. A finite element model was proposed to predict this distribution and the agreement between experimental and computational results represented its validity. The temperature distribution was uneven due to the internal temperature rise effect and the surface chilling effect during rolling. The initial sudden temperature rise and the overall temperature rise through rolling both exhibited proportional relationships with thickness reduction, while inverse correlations with initial temperature. The temperature drop of surface layer first increased and then decreased as the amount of thickness reduction increased during rolling. However it gradually increased as initial temperature increased, reaching a maximum of 147 degrees C. What's more, this surface chilling layer was only 1/6 of the total thickness and remained unchanged. (C) 2015 Elsevier B.V. All rights reserved.

引用

页码：286 / 294

页数：9

共 18 条

[1] Effect of temperature and strain rate on the deformation behavior and microstructure of a homogenized AZ31 magnesium alloy [J].

Bajargan, Govind ;

Singh, Gaurav ;

Sivakumar, D. ;

Ramamurty, U. .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2013, 579 :26-34

[2]

CHEN WC, 1993, IRONMAK STEELMAK, V20, P113

[3] FUNDAMENTAL PHENOMENA GOVERNING HEAT-TRANSFER DURING ROLLING [J].

CHEN, WC ;

SAMARASEKERA, IV ;

HAWBOLT, EB .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1993, 24 (06) :1307-1320

[4] THE THERMAL AND METALLURGICAL STATE OF STEEL STRIP DURING HOT-ROLLING .1. CHARACTERIZATION OF HEAT-TRANSFER [J].

DEVADAS, C ;

SAMARASEKERA, IV ;

HAWBOLT, EB .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1991, 22 (02) :307-319

[5] Effect of vertical rolling at various temperatures on subsequent multi-pass severe rolling of AZ31B alloy sheet [J].

Ding, Yunpeng ;

Le, Qichi ;

Zhang, Zhiqiang ;

Bao, Lei ;

Cao, Jing ;

Cui, Jianzhong .

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2013, 213 (12) :2101-2108

[6] Thermal modeling of strip across the transfer table in the hot rolling process [J].

Mansouri, N. ;

Mirhosseini, M. ;

Saboonchi, A. .

APPLIED THERMAL ENGINEERING, 2012, 38 :91-104

[7] Temperature rise during differential speed rolling [J].

Megantoro, R. B. ;

Loorentz ;

Ko, Y. G. .

JOURNAL OF ALLOYS AND COMPOUNDS, 2014, 586 :S254-S257

[8] An approximate method for computing the temperature distribution over material thickness during hot flat rolling [J].

Moon, C. H. ;

Lee, Y. .

INTERNATIONAL JOURNAL OF HEAT AND MASS TRANSFER, 2012, 55 (1-3) :310-315

[9] Superplasticity in a 7055 aluminum alloy processed by ECAE and subsequent isothermal rolling [J].

Nikulin, I ;

Kaibyshev, R ;

Sakai, T .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2005, 407 (1-2) :62-70

[10] Billet temperature rise during equal-channel angular pressing [J].

Nishida, Y ;

Ando, T ;

Nagase, M ;

Lim, SW ;

Shigematsu, I ;

Watazu, A .

SCRIPTA MATERIALIA, 2002, 46 (03) :211-216

← 1 2 →