The influence of Nb and Mo on the microstructure and mechanical properties of Ni-Cr-Fe GTAW welds

被引：33

作者：

Jeng, Sheng-Long ^{[1
]}

Chang, Yun-Han ^{[1
]}

机构：

[1] Inst Nucl Energy Res, Nucl Fuels & Mat Div, Tao Yuan 32546, Taiwan

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2012年 / 555卷

关键词：

Alloy; 52; Hot cracking; Ductility dip cracking; Niobium; Molybdenum; CRACKING;

D O I：

10.1016/j.msea.2012.06.017

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

This paper was intended to investigate the influence of Nb and Mo on the microstructure and mechanical properties of Ni-Cr-Fe welds. Alloy 52, Alloy 52M and two variants of customized weld metals with higher contents of Nb and Mo were used as the test weld metals. Welding was conducted with a machine gas tungsten arc welding (GTAW) process. The results showed that the welds were dominant with dendrites and interdendritic phases. In Alloy 52 weld, large TiCs/TiNs were the main interdendritic phases. Tiny TiCs/TiNs and Cr-carbides were found in the matrix and along the grain boundaries, respectively. With an increase of Nb/Mo content, large precipitates transformed from NbC/(Nb,Ti)C into Laves phases and their sizes increased. Tiny precipitates NbC/(Nb,Ti)C in the matrix turned into (Nb,Mo)/C when Mo was added. The precipitation of Cr-carbides along grain boundaries was reduced with the addition of Nb/Mo. The hardness measurements of the fusion zone increased proportionally with the contents of Nb and Mo. Tensile tests showed that Nb and Mo increased the tensile strength. Ductile dimples were the fracture feature observed with the weld specimens with lower Nb contents. (c) 2012 Elsevier B.V. All rights reserved.

引用

页码：1 / 12

页数：12

共 14 条

[1]

Bamford W., 2005, P 12 INT C ENV DEGR, P959

[2]

Folkhard E., 1987, Welding Metallurgy of stainless steels, DOI DOI 10.1007/978-3-7091-8965-8

[3]

Grimmel B., 2005, NUREG1823 NRC

[4] Hot Cracking Susceptibility of Ni-Base Alloy Dissimilar Metal Welds [J].

Hanninen, H. ;

Brederholm, A. ;

Saukkonen, T. .

HOT CRACKING PHENOMENA IN WELDS II, 2008, :171-191

[5]

Hood B.B., 1995, 7 INT S ENV DEGR MAT, P69

[6] Effects of nb on the microstructure and elevated-temperature mechanical properties of alloy 690-SUS 304L dissimilar welds [J].

Jeng, Sheng-Long ;

Lee, Hwa-Ten ;

Huang, Hunn-Yuan ;

Kuo, Roang-Ching .

MATERIALS TRANSACTIONS, 2008, 49 (06) :1270-1277

[7] The microstructure and fracture behavior of the dissimilar alloy 690-SUS 304L joint with various Nb addition [J].

Lee, HT ;

Jeng, SL ;

Kuo, TY .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2003, 34A (05) :1097-1105

[8] Ductility-Dip Cracking in High Chromium, Ni-Base Filler Metals [J].

Lippold, J. C. ;

Nissley, N. E. .

HOT CRACKING PHENOMENA IN WELDS II, 2008, :409-+

[9]

McIlree A., 2001, MRP57 EPRI

[10]

Nagano H., 1989, SUMITOMO SEARCH, V40, P57

← 1 2 →