Synthesis And Characterization of Soybean Oil Based Unsaturated Polyester Resin

被引：6

作者：

Qin, Yan ^{[1
]}

Jia, Jinrong ^{[1
]}

Zhao, Liang ^{[1
]}

Huang, Zhixiong ^{[1
]}

Zhao, Shiwei ^{[1
]}

Zhang, Guangwu ^{[1
]}

Dai, Bifang ^{[1
]}

机构：

[1] Wuhan Univ Technol, Dept Mat & Engn, Wuhan 430070, Peoples R China

来源：

BIOTECHNOLOGY, CHEMICAL AND MATERIALS ENGINEERING, PTS 1-3 | 2012年 / 393-395卷

关键词：

soybean oil; estification; reaction extent; side reaction; MECHANICAL-PROPERTIES;

D O I：

10.4028/www.scientific.net/AMR.393-395.349

中图分类号：

Q81 [生物工程学（生物技术）]; Q93 [微生物学];

学科分类号：

071005 ; 0836 ; 090102 ; 100705 ;

摘要：

A novel soybean oil monoglyceride based unsaturated polyester resin (SOMGUPR) was prepared using two step polymerization with soybean oil,glycerol,1.2-propanediol,maleric anhydride and phthalic anhydride. FT-IR spectroscopy,Gel Permeation Chromatography (GPC) and H-1-NMR spectroscopy were employed to study the chemical structure and molecular weight of this unsaturated polyester resin. The results show that 190 degrees C is the optimal temperature to controll the extent of estification reaction. The number-average molecular weight(Mn) decrease with the increasing value of n(glycerol):n(soybean) oil in SMOGUPR.Also,the side reaction between SOMG and maleric anhydride has not occured as evidenced by H-1-NMR spectroscopy.

引用

页码：349 / 353

页数：5

共 4 条

[1] Synthesis and characterization of polyester resins based on Nahar seed oil
Dutta, N
Karak, N
Dolui, SK
[J]. PROGRESS IN ORGANIC COATINGS, 2004, 49 (02) : 146 - 152
[2] Polymerization of maleic anhydride-modified plant oils with polyols
Eren, T
Küsefoglu, SH
Wool, R
[J]. JOURNAL OF APPLIED POLYMER SCIENCE, 2003, 90 (01) : 197 - 202
[3] Sheet molding compound resins from soybean oil: Thickening Behavior and mechanical properties
Lu, Jue
Wool, Richard P.
[J]. POLYMER ENGINEERING AND SCIENCE, 2007, 47 (09) : 1469 - 1479
[4] Mechanical properties of linseed oil monoglyceride maleate/styrene copolymers
Mosiewicki, M
Aranguren, MI
Borrajo, J
[J]. JOURNAL OF APPLIED POLYMER SCIENCE, 2005, 97 (03) : 825 - 836

← 1 →