Acoustic emission study of fatigue crack closure of physical short and long cracks for aluminum alloy LY12CZ

被引：56

作者：

Chang, H. ^{[1
]}

Han, E. H. ^{[1
]}

Wang, J. Q. ^{[1
]}

Ke, W. ^{[1
]}

机构：

[1] Chinese Acad Sci, Inst Met Res, Environm Corros Ctr, Shenyang 110016, Peoples R China

来源：

INTERNATIONAL JOURNAL OF FATIGUE | 2009年 / 31卷 / 03期

关键词：

Crack Closure; Physical short crack; Acoustic emission; Aluminum alloy LY12CZ; FINITE-ELEMENT-ANALYSIS; THRESHOLD;

D O I：

10.1016/j.ijfatigue.2008.08.008

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

Crack closure of physical short and long cracks of LY12CZ aluminum alloy during fatigue process was investigated using acoustic emission (AE) technique. Results showed that the effective fatigue crack growth curve (da/dN vs. Delta K(eff)) of physical short and long cracks obtained by the AE technique was consistent with the effective fatigue crack growth Curve at high stress ratio (R = 0.8), which implied that the AE technique Could measure the crack closure level, especially for physical short crack. The growth rate of physical short crack was Much higher than that of long crack at the same Delta K, and the lower crack Closure level of short crack was the main reason. (C) 2008 Elsevier Ltd. All rights reserved.

引用

页码：403 / 407

页数：5

共 22 条

[1] Prediction of fatigue crack growth rates using crack closure finite element analysis [J].

Alizadeh, Hassan ;

Simandjuntak, Sarinova ;

Smith, David ;

Pavier, Martyn .

INTERNATIONAL JOURNAL OF FATIGUE, 2007, 29 (9-11) :1711-1715

[2]

ALLIDAY MDH, 1981, J TEST EVAL, V9, P195

[3]

BACHMAN W, 1976, SOC ENV ENG, V2, P351

[4]

BANERJEE S, 1984, AFWALTR844031 AIR FO

[5]

Elber W., 1970, Engineering Fracture Mechanics, V2, P37, DOI 10.1016/0013-7944(70)90028-7

[6]

FLECK NA, 1984, 104 CUEDCMATSTR

[7]

HO CL, 1973, ASTM STP, V536, P5

[8] REVIEW ON CRACK CLOSURE FOR CONSTANT AMPLITUDE LOADING IN FATIGUE [J].

KUMAR, R .

ENGINEERING FRACTURE MECHANICS, 1992, 42 (02) :389-400

[9] THE ACOUSTIC-EMISSION MEASUREMENT OF CLEAVAGE INITIATION NEAR THE DUCTILE BRITTLE TRANSITION-TEMPERATURE IN STEEL [J].

LEE, CS ;

LIVNE, T ;

GERBERICH, WW .

SCRIPTA METALLURGICA, 1986, 20 (08) :1137-1140

[10] Precise determination of fatigue crack closure in Al alloys [J].

Lee, CS ;

Park, CG ;

Chang, YW .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1996, 216 (1-2) :131-138

← 1 2 3 →