Corrosion behaviour of extruded AM30 magnesium alloy under salt-spray and immersion environments

被引：70

作者：

Song, Weiwei ^{[1
]}

Martin, Holly J. ^{[1
]}

Hicks, Ayesha ^{[1
]}

Seely, Denver ^{[1
]}

Walton, Christopher A. ^{[1
]}

Lawrimore, William B., II ^{[1
]}

Wang, Paul T. ^{[1
]}

Horstemeyer, M. F. ^{[1
]}

机构：

[1] Mississippi State Univ, Ctr Adv Vehicular Syst, Mississippi State, MS 39762 USA

来源：

CORROSION SCIENCE | 2014年 / 78卷

关键词：

Magnesium; Alloy; Aluminium; Passive Films; Pitting Corrosion; ATMOSPHERIC CORROSION; PURE MAGNESIUM; AZ91; MG; QUANTIFICATION; CAST; MECHANISMS; MORPHOLOGY; CHLORIDE; FILMS;

D O I：

10.1016/j.corsci.2013.10.020

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The mechanisms associated with general, pitting, and filiform corrosion were quantified at various intervals for extruded AM30 magnesium alloy exposed to a cyclical salt spray and immersion environment. The three mechanisms were quantified using optical microscopy, laser profilometry, and SEM coupled with EDX for over 60 h of testing. General corrosion and pitting corrosion were more severe in the immersion environment, and filiform corrosion was more severe in the salt-spray environment. The presence of a sodium ion (Na+) diffusion region around the edge of the corrosion pits functioned as cathodic sites, accelerating the localised pitting corrosion rates in immersion environment. (C) 2013 Elsevier Ltd. All rights reserved.

引用

页码：353 / 368

页数：16

共 50 条

[41] Corrosion behaviour of microarc-oxidised magnesium alloy in Earle's balanced salt solution
Zhang, Junqing
Zhang, Lei
Wilke, Benjamin M.
Li, Weiping
Ning, Chengyun
Chowdhury, Tonoy
SURFACE INNOVATIONS, 2017, 5 (01) : 43 - 53
[42] Corrosion mechanism of line pipe steels (API X70 and X80 grades) under aggressive salt-spray exposure
Chinara, Manaswini
Ghosh, Rishav
Mukherjee, Subrata
Mondal, K.
MATERIALS CHEMISTRY AND PHYSICS, 2025, 339
[43] Electrochemical corrosion behaviour of plasma electrolytic oxidation coatings on AM50 magnesium alloy formed in silicate and phosphate based electrolytes
Liang, J.
Srinivasan, P. Bala
Blawert, C.
Stoermer, M.
Dietzel, W.
ELECTROCHIMICA ACTA, 2009, 54 (14) : 3842 - 3850
[44] High-speed deformation behaviour of 45° extruded magnesium alloy under quasi-in-situ conditions
Zhou, Le
Yan, Ruihua
Li, Yutian
Wang, Zhi
Wang, Feng
Wei, Ziqi
Mao, Pingli
Liu, Zheng
MATERIALS SCIENCE AND TECHNOLOGY, 2024, 40 (14) : 1069 - 1081
[45] The Influence of Ca2+ in Deicing Salt on the Chemistry of Corrosion Products Formed on AM50 Magnesium Alloy-Calcareous Deposition
Grabowski, Michael
Bluecher, Daniel
Korte, Michael
Virtanen, Sannakaisa
CORROSION, 2015, 71 (06) : 703 - 725
[46] Experimental study and 3D cellular automata simulation of corrosion pits on Q345 steel surface under salt-spray environment
Cui Chuanjie
Ma Rujin
Chen Airong
Pan Zichao
Tian Hao
CORROSION SCIENCE, 2019, 154 : 80 - 89
[47] Influence of glycerol on plasma electrolytic oxidation coatings evolution and on corrosion behaviour of coated AM50 magnesium alloy
Jangde, Ashutosh
Kumar, S.
Blawert, C.
CORROSION SCIENCE, 2019, 157 : 220 - 246
[48] Corrosion behaviour of AM60 magnesium alloys containing Ce or La under thin electrolyte layers. Part 1: Microstructural characterization and electrochemical behaviour
Liu, Wenjuan
Cao, Fahe
Chen, Anna
Chang, Linrong
Zhang, Jianqing
Cao, Chunan
CORROSION SCIENCE, 2010, 52 (02) : 627 - 638
[49] In-situ monitoring of the corrosion behaviour of austempered ductile iron (ADI) under cyclic salt spray exposure
Krawiec, H.
Vignal, V.
Lelito, J.
Krystianiak, A.
Ozga, P.
CORROSION SCIENCE, 2021, 185
[50] Influence of chloride ion concentration on the electrochemical corrosion behaviour of plasma electrolytic oxidation coated AM50 magnesium alloy
Liang, J.
Srinivasan, P. Bala
Blawert, C.
Dietzel, W.
ELECTROCHIMICA ACTA, 2010, 55 (22) : 6802 - 6811

← 1 2 3 4 5 →