Hot corrosion behaviour of (γ + α2)-Ti-46Al-8Nb (at.%) and α-Ti-6Al-1Mn (at.%) alloys

被引：41
|
作者：
Mitoraj-Krolikowska, Marzena [1 ]
Godlewska, Elzbieta [1 ]
机构：
[1] AGH Univ Sci & Technol, Al Mickiewicza 30, PL-30059 Krakow, Poland
来源：
CORROSION SCIENCE | 2017年 / 115卷
关键词：
Titanium; SEM; Hot corrosion; OXIDATION BEHAVIOR; HIGH-TEMPERATURE; TITANIUM ALUMINIDES; TIAL ALLOYS; INTERMETALLICS; DIFFUSION; ENVIRONMENT; SUPERALLOY; OXYGEN; AIR;
D O I：
10.1016/j.corsci.2016.11.006
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Hot corrosion behaviour of (gamma + alpha(2))-Ti-46Al-8Nb (at.%) and alpha-Ti-6Al-1 Mn (at.%) alloys was investigated in thermal cyclic conditions at 700, 800 and 900 degrees C. The samples were intentionally contaminated with Na2SO4 or NaCI or with a mixture of these. The corrosion rate was evaluated on the basis of mass change measurements. Degradation of materials was examined at the surface and on cross-sections by scanning electron microscopy (SEM). The chemical and phase composition of scale was determined with energy dispersive X-ray spectroscopy (EDS) and X-ray diffraction (XRD). It has been demonstrated that both (gamma+alpha(2))-Ti-46Al-8Nb (at.%) and alpha-Ti-6Al-1 Mn (at.%) are not resistant to hot corrosion. Remarkable mass changes of samples accompanied by intensive scale spallation was observed especially with sodium chloride deposit. (C) 2016 Elsevier Ltd. All rights reserved.
引用
收藏
页码：18 / 29
页数：12
相关论文
共 50 条
  • [31] EXPERIMENTAL STUDY OF COLUMNAR TO EQUIAXED TRANSITION DURING DIRECTIONAL SOLIDIFICATION OF INTERMETALLIC TI-46AL-8NB ALLOY
    Gabalcova, Zuzana
    Lapin, Juraj
    METAL 2009, CONFERENCE PROCEEDINGS, 2009, : 330 - 337
  • [32] Spray forming of Ti 48.9Al (at.%) and subsequent hot isostatic pressing and forging
    Gerlings, R
    Schimansky, FP
    Wegmann, G
    Zhang, JX
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2002, 326 (01): : 73 - 78
  • [33] Effects of mechanical alloying on the characteristics of a nanocrystalline Ti-50 at.%Al during hot pressing consolidation
    Farhang, Mohammad Reza
    Kamali, Ali Reza
    Nazarian-Samani, Masoud
    MATERIALS SCIENCE AND ENGINEERING B-ADVANCED FUNCTIONAL SOLID-STATE MATERIALS, 2010, 168 (1-3): : 136 - 141
  • [34] Effect of 2–6 at.% Mo addition on microstructural evolution of Ti-44Al alloy
    S.Z.Zhang
    Z.W.Song
    J.C.Han
    C.J.Zhang
    P.Lin
    D.D.Zhu
    F.T.Kong
    Y.Y.Chen
    Journal of Materials Science & Technology, 2018, 34 (07) : 1196 - 1204
  • [35] Microstructure evolution of directionally solidified Ti-46Al-8Nb alloy in the BaZrO3-based mould
    Li, Kai
    Chen, Guangyao
    Zhang, Hao
    Ali, Wajid
    Lu, Xionggang
    Li, Chonghe
    MATERIALS RESEARCH EXPRESS, 2018, 5 (11):
  • [36] Microstructure and oxidation behaviour of plasma-sprayed NiCoCrAlY coatings with and without Ta on Ti44Al6Nb1 Cr alloys
    Chen, Ruirun
    Gong, Xue
    Wang, You
    Qin, Gang
    Zhang, Nannan
    Su, Yanqing
    Ding, Hongsheng
    Guo, Jingjie
    Fu, Hengzhi
    CORROSION SCIENCE, 2018, 136 : 244 - 254
  • [37] Corrosion behaviour of Fe-Al(-Ti) alloys in steam
    Vogel, D.
    Hotar, A.
    Vogel, A.
    Palm, M.
    Renner, F. U.
    INTERMETALLICS, 2010, 18 (07) : 1375 - 1378
  • [38] Plasma enhanced paste aluminizing of Ti-45Al-2Nb-2Mn-1B with Al-Si alloys
    Rastkar, Ahmad Reza
    SURFACE & COATINGS TECHNOLOGY, 2015, 283 : 10 - 21
  • [39] The effect of oxygen content and cooling rate on phase transformations in directionally solidified intermetallic Ti-46Al-8Nb alloy
    Lapin, J.
    Gabalcova, Z.
    KOVOVE MATERIALY-METALLIC MATERIALS, 2008, 46 (04): : 185 - 195
  • [40] On the Microstructure and Properties of Nb-18Si-6Mo-5Al-5Cr-2.5W-1Hf Nb-Silicide Based Alloys with Ge, Sn and Ti Additions (at.%)
    Zhao, Jiang
    Utton, Claire
    Tsakiropoulos, Panos
    MATERIALS, 2020, 13 (20) : 1 - 37
12345