Microstructural evolution of a CoCrFeMnNi high-entropy alloy after swaging and annealing

被引:180
作者
Laplanche, G. [1 ]
Horst, O. [1 ]
Otto, F. [1 ]
Eggeler, G. [1 ]
George, E. P. [1 ]
机构
[1] Ruhr Univ Bochum, Inst Werkstoffe, D-44801 Bochum, Germany
关键词
Metals and alloys; Entropy; Microstructure; Mechanical properties; Scanning electron microscopy; SEM; STACKING-FAULT ENERGY; GRAIN-GROWTH; PHASE-STABILITY; SINGLE-PHASE; MECHANICAL-PROPERTIES; ELASTIC-MODULI; RECRYSTALLIZATION; BEHAVIOR; DEFORMATION; BOUNDARIES;
D O I
10.1016/j.jallcom.2015.05.129
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
The processing parameters which govern the evolution of microstructure and texture during rotary swaging and subsequent heat treatments were studied in an equiatomic single-phase CoCrFeMnNi high-entropy alloy. After vacuum induction melting and casting, the diameter of the 40 mm cast ingot was reduced at room temperature to a final diameter of 16.5 mm by rotary swaging (diameter reduction of 60%/area reduction of 80%) and the alloy was then annealed at different temperatures for 1 h. The resulting microstructures were analyzed using scanning electron microscopy, energy-dispersive X-ray spectroscopy, electron backscatter diffraction and correlated with results of microhardness measurements. It was found that the microhardness first increases slightly upon annealing below the recrystallization temperature but then drops steeply at higher annealing temperatures due to the onset of recrystallization. Special emphasis was placed on how the microstructure evolves with respect to the radial and longitudinal position in the rod. Finally, a combination of swaging and heat treatment parameters were identified that can produce CoCrFeMnNi high-entropy alloys with a homogeneous composition and grain size and almost no texture. (C) 2015 Published by Elsevier B.V.
引用
收藏
页码:548 / 557
页数:10
相关论文
共 43 条
[1]   Microstructure and texture evolution during annealing of equiatomic CoCrFeMnNi high-entropy alloy [J].
Bhattacharjee, P. P. ;
Sathiaraj, G. D. ;
Zaid, M. ;
Gatti, J. R. ;
Lee, Chi ;
Tsai, Che-Wei ;
Yeh, Jien-Wei .
JOURNAL OF ALLOYS AND COMPOUNDS, 2014, 587 :544-552
[2]   Microstructural development in equiatomic multicomponent alloys [J].
Cantor, B ;
Chang, ITH ;
Knight, P ;
Vincent, AJB .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 375 :213-218
[3]   Recrystallization and texture [J].
Doherty, RD .
PROGRESS IN MATERIALS SCIENCE, 1997, 42 (1-4) :39-58
[4]   COLD-ROLLED AND PRIMARY RECRYSTALLIZATION TEXTURES IN COLD-ROLLED SINGLE CRYSTALS OF SILICON IRON [J].
DUNN, CG .
ACTA METALLURGICA, 1954, 2 (02) :173-183
[5]   SECONDARY RECRYSTALLIZATION TEXTURES AND THEIR ORIGIN IN COLD-ROLLED SINGLE CRYSTALS OF SILICON IRON [J].
DUNN, CG .
ACTA METALLURGICA, 1953, 1 (02) :163-175
[6]   ON THE THEORY OF SECONDARY RECRYSTALLIZATION TEXTURE FORMATION IN FACE-CENTERED CUBIC METALS [J].
DUNN, CG .
ACTA METALLURGICA, 1954, 2 (03) :386-393
[7]   ON VARIATION OF WIRE TEXTURE WITH STACKING FAULT ENERGY IN FCC METALS AND ALLOYS [J].
ENGLISH, AT ;
CHIN, GY .
ACTA METALLURGICA, 1965, 13 (09) :1013-&
[8]   On the influence of thermomechanical treatments on the microstructure and phase transformation behavior of Ni-Ti-Fe shape memory alloys [J].
Frenzel, J. ;
Pfetzing, J. ;
Neuking, K. ;
Eggeler, G. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 481 (1-2 C) :635-638
[9]   Tensile properties of high- and medium-entropy alloys [J].
Gali, A. ;
George, E. P. .
INTERMETALLICS, 2013, 39 :74-78
[10]   A fracture-resistant high-entropy alloy for cryogenic applications [J].
Gludovatz, Bernd ;
Hohenwarter, Anton ;
Catoor, Dhiraj ;
Chang, Edwin H. ;
George, Easo P. ;
Ritchie, Robert O. .
SCIENCE, 2014, 345 (6201) :1153-1158