Engineering MXene surface with POSS for reducing fire hazards of polystyrene with enhanced thermal stability

High-performance MXene-based polymer nanocomposites are highly desirable for diverse industry applications due to their exceptional mechanical, thermal and other properties. Nevertheless, it remains an intractable challenge to create flame retardant polymer/MXene nanocomposites due to the difficulty to achieve uniform dispersion of MXenes. Here, we reported a facile strategy for the surface manipulation of two-dimensional titanium carbide nanosheets (Ti3C2Tx) with 3-aminopropylheptaisobutyl-polyhedral oligomeric silsesquioxane (AP-POSS) (POSS-Ti3C2Tx) through electrostatic interactions. The POSS-Ti3C2Tx is steadily dispersed in many polar solvents. Upon incorporated into polystyrene (PS), the combined effect of AP-POSS and MXene makes the resultant PS nanocomposites exhibit significantly improved thermal and thermoxidative stability, e.g. 22 degrees C and 39 degrees C increases in the temperature at 5 wt% mass loss under nitrogen and air, respectively. Meanwhile, a 39.1 % reduction in the peak heat release rate, a respective 54.4 % and 35.6 % reduction in the peak CO production rate and the peak CO2 production rate was achieved, which are superior to those of its own and previous counter-parts. This outstanding fire safety is attributed to the combination of adsorption, catalytic and barrier effects of POSS-Ti3C2Tx. Hence, as-designed functionalized MXenes can be effectively applied in PS to formulate multifunctional polymer nanocomposites attractive for wide potential applications.