Tribological behaviours of PVD TiN and TiCN coatings in artificial seawater

被引：168
作者：
Shan, Lei [1 ,2 ]
Wang, Yongxin [1 ]
Li, Jinlong [1 ]
Li, He [1 ]
Wu, Xuedong [1 ]
Chen, Jianmin [1 ]
机构：
[1] Chinese Acad Sci, Ningbo Inst Mat Technol & Engn, Ningbo Key Lab Marine Protect Mat, Ningbo 315201, Zhejiang, Peoples R China
[2] Zhejiang Textile & Fash Coll, Dept Mech, Ningbo 315211, Zhejiang, Peoples R China
来源：
SURFACE & COATINGS TECHNOLOGY | 2013年 / 226卷
基金：
中国国家自然科学基金;
关键词：
TIN and TiCN coatings; Friction; Wear; Tribocorrosion; Artificial seawater; CORROSION-RESISTANCE; TITANIUM NITRIDE; ION-IMPLANTATION; STAINLESS-STEEL; PERFORMANCE; HARDNESS; FILMS; WATER; WEAR; MICROSTRUCTURE;
D O I：
10.1016/j.surfcoat.2013.03.034
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
To improve the tribological performance of sea frictional components, TiN and TiCN coatings, were used for surface protection of the components. The coatings were deposited on stainless steel and WC cemented carbides by arc ion plating. The coating topography was observed using scanning electron microscopy (SEM), and the composition and structure were analyzed by energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD). Hardness and adhesion force were tested by nanoindentation and scratch tester, respectively. The friction and wear properties of the TIN and TiCN coatings were investigated by ball-on-disk tribometer in air, distilled water and artificial seawater. The results showed that both the TiCN and TiN coatings had a strong (111) preferred orientation. The friction coefficients of the coatings in distilled water and artificial seawater were lower than those in air. This indicates the influence of aqueous solutions on the friction coefficient due to the lubricative film formed on the coatings. However, the wear loss of the coatings in artificial seawater was larger than those in air and distilled water, this demonstrates a positive synergism between corrosion and wear in artificial seawater. The TiCN coating shows the best wear resistance in the artificial seawater. (c) 2013 Elsevier B.V. All rights reserved.
引用
收藏
页码：40 / 50
页数：11
相关论文
共 27 条
[1]   Study of the corrosion resistance and in vitro biocompatibility of PVD TiCN-coated AISI 316 L austenitic stainless steel for orthopedic applications [J].
Antunes, R. A. ;
Rodas, A. C. D. ;
Lima, N. B. ;
Higa, O. Z. ;
Costa, I. .
SURFACE & COATINGS TECHNOLOGY, 2010, 205 (07) :2074-2081
[2]   Properties and performance of commercial TiCN coatings. Part 1: coating architecture and hardness modelling [J].
Bull, SJ ;
Bhat, DG ;
Staia, MH .
SURFACE & COATINGS TECHNOLOGY, 2003, 163 :499-506
[3]   Properties and performance of commercial TiCN coatings. Part 2: tribological performance [J].
Bull, SJ ;
Bhat, DG ;
Staia, MH .
SURFACE & COATINGS TECHNOLOGY, 2003, 163 :507-514
[4]   Microstructure and hardness of hollow cathode discharge ion-plated titanium nitride film [J].
Chen, CT ;
Song, YC ;
Yu, GP ;
Huang, JH .
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 1998, 7 (03) :324-328
[5]   Tribological properties of bronze-graphite composites under sea water condition [J].
Cui, Gongjun ;
Bi, Qinling ;
Zhu, Shengyu ;
Yang, Jun ;
Liu, Weimin .
TRIBOLOGY INTERNATIONAL, 2012, 53 :76-86
[6]   Effects of vanadium ion implantation on microstructure, mechanical and tribological properties of TiN coatings [J].
Deng, Bin ;
Tao, Ye ;
Guo, Deliang .
APPLIED SURFACE SCIENCE, 2012, 258 (22) :9080-9086
[7]  
Feng HP, 2003, MAT SCI ENG A-STRUCT, V347, P123, DOI 10.1016/S0921-5093(02)00578-6
[8]  
Hanawa T, 1998, J BIOMED MATER RES, V40, P530, DOI 10.1002/(SICI)1097-4636(19980615)40:4<530::AID-JBM3>3.3.CO
[9]  
2-H
[10]   Influence of residual stresses on the mechanical properties of TiCxN1-x (x=0, 0.15, 0.45) thin films deposited by arc evaporation [J].
Karlsson, L ;
Hultman, L ;
Sundgren, JE .
THIN SOLID FILMS, 2000, 371 (1-2) :167-177
123