Fatigue strength improvement of an aluminum alloy with a crack-like surface defect using shot peening and cavitation peening

被引：63
作者：
Takahashi, Koji [1 ]
Osedo, Hiroko [1 ]
Suzuki, Takaya [1 ]
Fukuda, Shinsaku [2 ]
机构：
[1] Yokohama Natl Univ, 79-5 Tokiwadai, Yokohama, Kanagawa 2408501, Japan
[2] Isuzu Motors Ltd, Japan 8, Fujisawa, Kanagawa 2520881, Japan
来源：
ENGINEERING FRACTURE MECHANICS | 2018年 / 193卷
关键词：
Cavitation peening; Shot peening; Fatigue strength; Surface defect; Aluminum alloy; RESIDUAL-STRESSES; PEENED SPECIMENS; BLUNT NOTCHES; STEEL; LIMIT; LIFE; SHARP; HOLE;
D O I：
10.1016/j.engfracmech.2018.02.013
中图分类号：
O3 [力学];
学科分类号：
08 ; 0801 ;
摘要：
The effects of shot peening (SP) and cavitation peening (CP) on the bending fatigue strength of the 7075 aluminum alloy with a crack-like surface defect were investigated. Test specimens containing a small semicircular slit were subjected to SP and CP. Bending fatigue tests were conducted on the specimens to determine the fatigue strength and critical depth (ac) of the semicircular slit that can be rendered harmless by peening. The results indicated that fatigue strengths increased by peening and that semicircular slits less than 0.1 and 0.2mm in depth were rendered harmless by SP and CP, respectively. The ac values estimated based on fracture mechanics were similar to experimental values, indicating that ac was affected by the distribution of the compressive residual stress induced by peening.
引用
收藏
页码：151 / 161
页数：11
相关论文
共 28 条
  • [1] Acceptable Defect Size Research Committee, 2008, Tran Jpn Soc Spring Engineer, V53, P57
  • [2] Residual stresses reconstruction in shot peened specimens containing sharp and blunt notches by experimental measurements and finite element analysis
    Benedetti, M.
    Fontanari, V.
    Winiarski, B.
    Allahkarami, M.
    Hanan, J. C.
    [J]. INTERNATIONAL JOURNAL OF FATIGUE, 2016, 87 : 102 - 111
  • [3] High- and very high-cycle plain fatigue resistance of shot peened high-strength aluminum alloys: The role of surface morphology
    Benedetti, M.
    Fontanari, V.
    Bandini, M.
    Savio, E.
    [J]. INTERNATIONAL JOURNAL OF FATIGUE, 2015, 70 : 451 - 462
  • [4] Notch fatigue behaviour of shot peened high-strength aluminium alloys: Experiments and predictions using a critical distance method
    Benedetti, M.
    Fontanari, V.
    Santus, C.
    Bandini, M.
    [J]. INTERNATIONAL JOURNAL OF FATIGUE, 2010, 32 (10) : 1600 - 1611
  • [5] Reverse bending fatigue of shot peened 7075-T651 aluminium alloy: The role of residual stress relaxation
    Benedetti, M.
    Fontanari, V.
    Scardi, P.
    Ricardo, C. L. A.
    Bandini, M.
    [J]. INTERNATIONAL JOURNAL OF FATIGUE, 2009, 31 (8-9) : 1225 - 1236
  • [6] Fatigue behavior of nitrided and shot peened steel with artificial small surface defects
    Fernandez-Pariente, I.
    Bagherifard, S.
    Guagliano, M.
    Ghelichi, R.
    [J]. ENGINEERING FRACTURE MECHANICS, 2013, 103 : 2 - 9
  • [7] Fueki R., 2015, Materials Sciences and Applications, V6, P500, DOI DOI 10.4236/msa.2015.66053
  • [8] Cavitation peening to improve the fatigue strength of nitrocarburized steel
    Fukuda, S.
    Matsui, K.
    Ishigami, H.
    Ando, K.
    [J]. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2008, 31 (10) : 857 - 862
  • [9] Fukuda S., 2009, T JAPAN SOC SPRING E, V54, P1
  • [10] CRACK-PROPAGATION IN THE PRESENCE OF SHOT-PEENING RESIDUAL-STRESSES
    HAMMOND, DW
    MEGUID, SA
    [J]. ENGINEERING FRACTURE MECHANICS, 1990, 37 (02) : 373 - 387
123