Microstructure and properties of Bi-2223/Ag/Ni tapes

被引：7

作者：

Li Mingya ^{[1
]}

Ye Chengli ^{[1
]}

Liu Jun ^{[1
]}

机构：

[1] NE Univ Qinhuangdao, Sch Resources & Mat, Qinhuangdao 066004, Peoples R China

来源：

RARE METALS | 2012年 / 31卷 / 06期

关键词：

Bi-2223/Ag/Ni tapes; heat treatment; microstructure; critical current; TEMPERATURE; (BI; PB)-2223; FABRICATION;

D O I：

10.1007/s12598-012-0557-9

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

To reduce the production cost of Bi-2223 superconducting tapes, Bi-2223/Ag/Ni tapes were fabricated by the powder-in-tube process. The effect of heat treatment on the microstructure and critical current of the Bi-2223/Ag/Ni tapes were studied. The phase compositions of the samples were characterized using XRD. The microstructure was observed using SEM. Experimental results indicate that higher temperature is more conducive to the formation of Bi-2223 phase at an atmosphere of 8.5% O-2. After the two-step heat treatment, the critical current of samples is about 67.5 A.

引用

页码：556 / 559

页数：4

共 15 条

[1]

Andersen N.H., 2008, J PHYS, V97, P1

[2] Fabrication and Properties of Ag-Ni Bimetallic Sheathed (Bi,Pb)-2223 Tapes [J].

Chen, X. P. ;

Yu, X. W. ;

Liu, M. ;

Li, M. Y. ;

Sun, H. B. ;

Liu, Q. .

JOURNAL OF SUPERCONDUCTIVITY AND NOVEL MAGNETISM, 2012, 25 (05) :1501-1507

[3] Growth kinetics study of the (Bi,Pb)2Sr2Ca2Cu3O10 grains in Ag/Ni composite-sheathed tapes [J].

Chen, Xingpin ;

Yu, Xiaowei ;

Zhang, Jingpeng ;

Li, Mingya ;

Sun, Haibo ;

Liu, Qing .

SOLID STATE SCIENCES, 2011, 13 (12) :2165-2171

[4] Composite metallic sheathes:: the key to low-cost, high strength (Bi, Pb)2Sr2Ca2Cu3O10-based tapes? [J].

Grivel, J-C .

SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2007, 20 (10) :1059-1064

[5] Power application of superconductivity technology in China [J].

Han, Z ;

Hu, XH .

SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2006, 19 (03) :S109-S113

[6]

Kurusu T, 2004, IEEE T APPL SUPERCON, V14, P393, DOI [10.1109/TASC.2004.829679, 10.1109/tasc.2004.829679]

[7] Phase evolution of lead oxide compounds corresponding with oxygen release and absorption processes of BSCCO powders during heat treatment [J].

Li, MY ;

Chen, XP ;

Qu, TM ;

Liu, Q ;

Han, Z .

SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2004, 17 (02) :249-255

[8] Fabrication and characterization of SmO0.7F0.2FeAs bulk with a transition temperature of 56.5 K [J].

Liu Zhiyong ;

Ma Lin ;

Zhao Junjing ;

Yan Binjie ;

Suo Hongli .

RARE METALS, 2011, 30 (05) :496-500

[9] Verification tests of a 66 kV HTSC cable system for practical use (first cooling tests) [J].

Masuda, T ;

Kato, T ;

Yumura, H ;

Watanabe, M ;

Ashibe, Y ;

Ohkura, K ;

Suzawa, C ;

Hirose, M ;

Isojima, S ;

Matsuo, K ;

Honjo, S ;

Mimura, T ;

Kuramochi, T ;

Takahashi, Y ;

Suzuki, H ;

Okamoto, T .

PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2002, 378 (PART 2) :1174-1180

[10] Highlights of coated conductor development in Japan [J].

Teranishi, R ;

Izumi, T ;

Shiohara, Y .

SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2006, 19 (03) :S4-S12

← 1 2 →