Improvement on direct ethanol fuel cell performance by using doped-Nafion® 117 membranes with Pt and Pt-Ru nanoparticles

Nafion (R) 117 membranes doped with Pt (4 x 10(-4) mol L-1 or 8 x 10(-4) mol L-1 H2PtCl6 solution), and with Pt-Ru (4 x 10(-4) mol L-1 H2PtCl6 and 2 x 10(-4) mol L-1 RuCl3 solutions) nanoparticles have been synthesized using a simple and scalable absorption-reduction method. The chemical integrity of the membranes was confirmed by C-13 and F-19 solid-state NMR. The pore microstructure of the membranes was preserved after the doping process, according to SAXS measurements. The tests of the direct ethanol fuel cells (DEFC) performance at 90 degrees C exhibited up to 38% and 56% increase at the maximum power densities for Pt doped-Nafion (R) membrane from lower and higher concentration of H2PtCl6 solution, respectively, compared to bare Nafion membranes. Additionally, a Pt-Ru doped-membrane tested at 110 degrees C exhibited the highest power density. Such superior performances may be attributed to a synergistic effect between the extra amount of active catalytic sites inside the pore structure for the electrochemical oxidation of ethanol, thus preventing ethanol crossover, and the excellent proton migration properties conferred by the pore microstructure of Nafion (R). These results demonstrate that the doped-Nafion (R) membrane has a good capacity to improve the performance of DEFC, and provided further clarification on the synthesis process of polymer electrolyte doped-membranes in fuel cell technology. Copyright (C) 2013, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.