Effect of ceramics coating using sol-gel processing on corrosion resistance and age hardening of AZ80 magnesium alloy substrate

被引：29

作者：

Harada, Yohei ^{[1
]}

Kumai, Shinji ^{[1
]}

机构：

[1] Tokyo Inst Technol, Dept Mat Sci & Engn, Midori Ku, Yokohama, Kanagawa 2268502, Japan

来源：

SURFACE & COATINGS TECHNOLOGY | 2013年 / 228卷

关键词：

Sol-gel processing; AZ80 magnesium alloy; Ceramic coating; Age hardening; Corrosion resistance; SINTERING TEMPERATURE; PROTECTION; BEHAVIOR; AZ91D; ADDITIONS; ALUMINUM; OXIDE;

D O I：

10.1016/j.surfcoat.2013.04.004

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Extruded plates of AZ80 magnesium alloy were coated with CeO2 and/or MgO ceramics by sol-gel processing. We investigated the effects of heat treatment conditions, under which the ceramic thin film was formed, on the mechanical properties and corrosion resistance of the substrates. Single layer (CeO2 or MgO) and double layer (CeO2/MgO) ceramic thin films were successfully formed from precursor solution by the sol-gel processing under optimal heat treatment, in which the AZ80 original substrates were age-hardened. The corrosion resistance of AZ80 magnesium alloy substrates evaluated by the salt water immersion test was found to be improved by ceramic coating and microstructural change of the original substrate during coating process. The double layer ceramic coating was superior to the single layer coatings in terms of corrosion resistance. The acquisition of corrosion resistance in AZ80 magnesium alloy substrates could be applied simultaneously by sol-gel processing, while the substrates were age-hardened by the heat treatment (C) 2013 Elsevier B.V. All rights reserved.

引用

页码：59 / 67

页数：9

共 29 条

[1] The effect of PVD coatings on the corrosion behaviour of AZ91 magnesium alloy [J].

Altun, Hikmet ;

Sen, Sadri .

MATERIALS & DESIGN, 2006, 27 (10) :1174-1179

[2]

[Anonymous], 2003, JIS HDB, P302

[3] Corrosion protection of AZ91 magnesium alloy by anodizing in niobium and zirconium-containing electrolytes [J].

Ardelean, H. ;

Frateur, I. ;

Zanna, S. ;

Atrens, A. ;

Marcus, P. .

CORROSION SCIENCE, 2009, 51 (12) :3030-3038

[4] Corrosion behaviour of AZ91D and AM50 magnesium alloys with Nd and Gd additions in humid environments [J].

Arrabal, R. ;

Matykina, E. ;

Pardo, A. ;

Merino, M. C. ;

Paucar, K. ;

Mohedano, M. ;

Casajus, P. .

CORROSION SCIENCE, 2012, 55 :351-362

[5] Effects of titanium addition on mechanical and corrosion behaviours of AZ91 magnesium alloy [J].

Candan, S. ;

Unal, M. ;

Koc, E. ;

Turen, Y. ;

Candan, E. .

JOURNAL OF ALLOYS AND COMPOUNDS, 2011, 509 (05) :1958-1963

[6] Deposition of aluminium on magnesium by a CVD process [J].

Christoglou, C ;

Voudouris, N ;

Angelopoulos, GN ;

Pant, M ;

Dahl, W .

SURFACE & COATINGS TECHNOLOGY, 2004, 184 (2-3) :149-155

[7] Improvement in stannate chemical conversion coatings on AZ91 D magnesium alloy using the potentiostatic technique [J].

Elsentriecy, Hassan H. ;

Azumi, Kazuhisa ;

Konno, Hidetaka .

ELECTROCHIMICA ACTA, 2007, 53 (02) :1006-1012

[8]

Fukuzaki M., 2005, Journal of Japan Institute of Light Metals, V55, P389, DOI 10.2464/jilm.55.389

[9] The corrosion and wear resistances of magnesium alloy (LZ91) electroplated with copper and followed by 1 μm-thick chromium deposits [J].

Huang, Ching An ;

Lin, Che Kuan ;

Yeh, Yu Hu .

THIN SOLID FILMS, 2011, 519 (15) :4774-4780

[10] Aging behaviour and precipitate morphologies in Mg-7.7Al-0.5Zn-0.3Mn (wt.%) alloy [J].

Lai, Wei-Jen ;

Li, Yi-Yun ;

Hsu, Yung-Fu ;

Trong, Shan ;

Wang, Wen-Hsiung .

JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 476 (1-2) :118-124

← 1 2 3 →