Oxidation behavior of the directionally solidified Ni-base superalloy DS951 in air

被引：15
|
作者：
Huang, L [1 ]
Sun, XF [1 ]
Guan, HR [1 ]
Hu, ZQ [1 ]
机构：
[1] Chinese Acad Sci, Inst Met Res, Superalloy Dept, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China
来源：
OXIDATION OF METALS | 2005年 / 64卷 / 5-6期
关键词：
Ni-base superalloy; DS951; oxidation; kinetics; microstructure;
D O I：
10.1007/s11085-005-8529-1
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The isothermal oxidation behavior at 1000, 1050 and 1100 degrees C and the cyclic oxidation behavior at 1000 degrees C of the directionally solidified Ni-base superalloy DS951 were investigated. The oxidized samples were characterized by SEM, EDAX, XRD. The alloy DS951 obeyed a two-stage parabolic rate law during isothermal oxidation at 1000-1100 degrees C. In cyclic conditions, the alloy showed no weight loss even after 1100 cycles. Cross-sectional examination revealed the development of faceted and needle-shaped AlN precipitates in the alloy subsurface region during cyclic oxidation, while no internal corrosion products were found in isothermal tests. Furthermore, a selective oxidation of MC carbides (M was predominately niobium with some chromium and tungsten) was observed along alloy grain boundaries and in interdendritic areas.
引用
收藏
页码：303 / 318
页数：16
相关论文
共 50 条
  • [1] Oxidation Behavior of the Directionally Solidified Ni-base Superalloy DS951 in Air
    L. Huang
    X. F. Sun
    H. R. Guan
    Z. Q. Hu
    Oxidation of Metals, 2005, 64 : 303 - 318
  • [2] Isothermal Oxidation Behavior of a New Directionally Solidified Ni-base Superalloy in Air at Different Temperature
    Wang, Lei
    Huang, Yan
    Zhao, Zhuo
    Liu, Yang
    Wu, Jiantao
    Yan, Ping
    PRICM 7, PTS 1-3, 2010, 654-656 : 538 - +
  • [3] High cycle fatigue behavior of a directionally solidified Ni-base superalloy DZ951
    Chu Zhaokuang
    Yu Jinjiang
    Sun Xiaofeng
    Guan Hengrong
    Hu Zhuangqi
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 496 (1-2): : 355 - 361
  • [4] Thermomechanical fatigue behavior of a directionally solidified Ni-base superalloy
    Shenoy, MM
    Gordon, AP
    McDowell, DL
    Neu, RW
    JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 2005, 127 (03): : 325 - 336
  • [5] High temperature low cycle fatigue behavior of a directionally solidified Ni-base superalloy DZ951
    Chu Zhaokuang
    Yu Jinjiang
    Sun Xiaofeng
    Guan Hengrong
    Hu Zhuangqi
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 488 (1-2): : 389 - 397
  • [6] Tensile property and deformation behavior of a directionally solidified Ni-base superalloy
    Chu, Zhaokuang
    Yu, Jinjiang
    Sun, Xiaofeng
    Guan, Hengrong
    Hu, Zhuangqi
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 527 (12): : 3010 - 3014
  • [7] Corrosion kinetics of a directionally solidified Ni-base superalloy
    Gordon, Ali P.
    Trexler, Matthew D.
    Neu, Richard W.
    Sanders, Thomas J.
    McDowell, David L.
    ACTA MATERIALIA, 2007, 55 (10) : 3375 - 3385
  • [8] High-Temperature Creep Deformation and Fracture Behavior of a Directionally Solidified Ni-Base Superalloy DZ951
    Chu, Zhaokuang
    Yu, Jinjiang
    Sun, Xiaofeng
    Guan, Hengrong
    Hu, Zhuangqi
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2009, 40A (12): : 2927 - 2937
  • [9] High-Temperature Creep Deformation and Fracture Behavior of a Directionally Solidified Ni-Base Superalloy DZ951
    Zhaokuang Chu
    Jinjiang Yu
    Xiaofeng Sun
    Hengrong Guan
    Zhuangqi Hu
    Metallurgical and Materials Transactions A, 2009, 40 : 2927 - 2937
  • [10] High temperature creep and fracture behavior of a directionally solidified Ni-base superalloy
    Yuan, C
    Guo, JT
    Wang, SH
    Yang, HC
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 1998, 14 (03) : 219 - 225
12345