Investigating the effects of aging and loading rate on low-temperature cracking resistance of core-based asphalt samples using semi-circular bending test

In this study, the asphalt concrete (AC) cracking resistance was examined at 15 degrees C, under model loading using semi-circular bending test (SCB). The SCB samples were prepared through pavement coring under the same conditions (i.e. mix design, passing traffic volume and, weather) with varying years of service life. First, the effect of asphalt aging on its cracking resistance was evaluated using field-aged AC cores. Second, the effect of loading rate on fracture parameters of SCB samples was examined using two different rates. Evaluating the load-displacement curves obtained from test results showed that the asphalt mixtures behaved as a linear elastic material at low temperature. Also, an increase in the pavement's life led to a significant decrease in failure deformation, fracture energy and critical energy release rate of the samples. Moreover, by increasing loading rate, the samples' peak load increased; however, fracture energy and failure deformation decreased. (C) 2016 Elsevier Ltd. All rights reserved.