A study on the susceptibility of high strength tempered martensite steels to hydrogen embrittlement (HE) based on incremental step load (ISL) testing methodology

被引:28
作者
Das, Tuhin [1 ]
Rajagopalan, Sriraman K. [1 ,2 ]
Brahimi, Salim V. [1 ,2 ]
Wang, Xiang [3 ]
Yue, Stephen [1 ]
机构
[1] McGill Univ, Dept Min & Mat Engn, Montreal, PQ H3A 0C5, Canada
[2] IBECA Technol Corp, Montreal, PQ H3H 1A8, Canada
[3] McMaster Univ, Dept Mat Sci & Engn, Hamilton, ON L8S 4L7, Canada
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2018年 / 716卷
基金
加拿大自然科学与工程研究理事会;
关键词
Hydrogen embrittlement; Material susceptibility; Incremental step load test; Transmission electron microscopy; Thermal desorption analysis; LOW-ALLOY STEELS; THERMAL-DESORPTION; DELAYED-FRACTURE; PIPELINE STEELS; DIFFUSION; INCLUSIONS; MECHANISM; PRESSURE; METALS; IRON;
D O I
10.1016/j.msea.2018.01.032
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Incremental step load (ISL) technique was used to determine the material susceptibility of three different grades of tempered martensite steels 35CrMo4, 41Cr4 and 36NiCrMo4 to hydrogen embrittlement (HE). In addition to testing the steel grades in air, the environmental hydrogen embrittlement susceptibilities (EHE) of each material were determined by in-situ charging of hydrogen at three different cathodic potentials -0.85 V-SCE, -1V(SCE) and -1.2V(SCE) to obtain the entire threshold curves for these materials. Overall investigation implies that 35CrMo4 is more susceptible than 41Cr4 and 36NiCrMo4. The fracture surface morphology in case of 35CrMo4 is entirely intergranular at -1V(SCE) and -1.2V(SCE) showing the severity of embrittlement. The higher matrix-cementite interfaces along with high cementite and low manganese sulphide (MnS) inclusion content of 36NiCrMo4 influencing the hydrogen transport kinetics within the material are responsible for the lower material susceptibility. The thermal desorption analyses (TDA) further corroborate the observations.
引用
收藏
页码:189 / 207
页数:19
相关论文
共 65 条
  • [1] Quantitative determination of hydrogen in solids by gas chromatography
    Addach, H
    Berçot, P
    Wery, M
    Rezrazi, X
    [J]. JOURNAL OF CHROMATOGRAPHY A, 2004, 1057 (1-2) : 219 - 223
  • [2] Studies of Evaluation of Hydrogen Embrittlement Property of High-Strength Steels with Consideration of the Effect of Atmospheric Corrosion
    Akiyama, Eiji
    Wang, Maoqiu
    Li, Songjie
    Zhang, Zuogui
    Kimura, Yuuji
    Uno, Nobuyoshi
    Tsuzaki, Kaneaki
    [J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2013, 44A (03): : 1290 - 1300
  • [3] Andrews K., 1971, Interpretation of Electron Diffraction Patterns, V2nd
  • [4] ASTM, 2012, F162412 ASTM
  • [5] ASTM, 2010, F51910 ASTM
  • [6] ELECTROCHEMICAL STUDIES OF HYDROGEN DIFFUSION AND PERMEABILITY IN NI
    ATRENS, A
    MEZZANOTTE, D
    FIORE, NF
    GENSHAW, MA
    [J]. CORROSION SCIENCE, 1980, 20 (05) : 673 - 684
  • [7] HYDROGEN-ENHANCED LOCALIZED PLASTICITY - A MECHANISM FOR HYDROGEN-RELATED FRACTURE
    BIRNBAUM, HK
    SOFRONIS, P
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1994, 176 (1-2): : 191 - 202
  • [8] Bockris J. M., 1970, MODERN ELECTROCHEMIS
  • [9] EQUIVALENT PRESSURE OF MOLECULAR HYDROGEN IN CAVITIES WITHIN METALS IN TERMS OF OVERPOTENTIAL DEVELOPED DURING EVOLUTION OF HYDROGEN
    BOCKRIS, JOM
    SUBRAMAN.PK
    [J]. ELECTROCHIMICA ACTA, 1971, 16 (12) : 2169 - &
  • [10] BONISZEWSKI T, 1967, BR WELD J, V14, P321