Grain boundary selective oxidation and intergranular stress corrosion crack growth of high-purity nickel binary alloys in high-temperature hydrogenated water

被引：48

作者：

Bruemmer, S. M. ^{[1
]}

Olszta, M. J. ^{[1
]}

Toloczko, M. B. ^{[1
]}

Schreiber, D. K. ^{[1
]}

机构：

[1] Pacific Northwest Natl Lab, Energy & Environm Directorate, Richland, WA 99354 USA

来源：

CORROSION SCIENCE | 2018年 / 131卷

关键词：

Nickel; Alloy; TEM; Intergranular corrosion; Stress corrosion; Selective oxidation; ATOM-PROBE TOMOGRAPHY; INTERNAL OXIDATION; ENVIRONMENTAL CRACKING; ELECTRON-MICROSCOPY; POURBAIX DIAGRAMS; CHROMIUM-ALLOYS; MECHANISM; SYSTEMS; CR; DIFFUSION;

D O I：

10.1016/j.corsci.2017.11.024

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The effects of alloying elements in Ni-5at%X binary alloys on intergranular (IG) corrosion and stress corrosion cracking (SCC) have been assessed in 300-360 degrees C hydrogenated water at the Ni/NiO stability line. Alloys with Cr or Al additions exhibited grain boundary oxidation and IGSCC, while localized degradation was not observed for pure Ni, Ni-Cu or Ni-Fe alloys. Environment-enhanced crack growth was determined by comparing the response in water and N-2 gas. Results demonstrate that selective grain boundary oxidation of Cr and Al promoted IGSCC of these Ni alloys in hydrogenated water.

引用

页码：310 / 323

页数：14

共 59 条

[51] Swisher J.H., 1971, OXIDATION METALS ALL, P235
[52] High-resolution characterization of intergranular attack and stress corrosion cracking of Alloy 600 in high-temperature primary water
Thomas, LE
Bruemmer, SM
[J]. CORROSION, 2000, 56 (06) : 572 - 587
[53] In situ site-specific specimen preparation for atom probe tomography
Thompson, K.
Lawrence, D.
Larson, D. J.
Olson, J. D.
Kelly, T. F.
Gorman, B.
[J]. ULTRAMICROSCOPY, 2007, 107 (2-3) : 131 - 139
[54] Toloczko M.B., 2016, NUREGCR7103, V3
[55] QUANTITATIVE MODEL OF HYDROGEN INDUCED GRAIN-BOUNDARY CRACKING
VANLEEUWEN, HP
[J]. CORROSION, 1973, 29 (05) : 197 - 204
[56] Vermilyea D.A., 1973, P C STRESS CORR CRAC, P208
[57] ENHANCED DIFFUSION OF OXYGEN DURING INTERNAL OXIDATION OF NICKEL-BASE ALLOYS
WHITTLE, DP
SHIDA, Y
WOOD, GC
STOTT, FH
BASTOW, BD
[J]. PHILOSOPHICAL MAGAZINE A-PHYSICS OF CONDENSED MATTER STRUCTURE DEFECTS AND MECHANICAL PROPERTIES, 1982, 46 (06): : 931 - 949
[58] MECHANISM OF OXIDATION OF DILUTE NICKEL - CHROMIUM ALLOYS
WOOD, GC
HODGKIES.T
[J]. NATURE, 1966, 211 (5056) : 1358 - &
[59] THE HIGH-TEMPERATURE INTERNAL OXIDATION AND INTERGRANULAR OXIDATION OF NICKEL-CHROMIUM ALLOYS
WOOD, GC
STOTT, FH
WHITTLE, DP
SHIDA, Y
BASTOW, BD
[J]. CORROSION SCIENCE, 1983, 23 (01) : 9 - 25

← 1 2 3 4 5 6 →