The Influence of Hydrogen on the Low Cycle Fatigue Behavior of Medium Strength 3.5NiCrMoV Steel Studied Using Notched Specimens

被引：9
作者：
Liu, Qian [1 ]
Atrens, Andrej [1 ]
机构：
[1] Univ Queensland, Mat Engn, St Lucia, Qld 4072, Australia
来源：
ADVANCED ENGINEERING MATERIALS | 2018年 / 20卷 / 02期
基金：
澳大利亚研究理事会;
关键词：
Hydrogen; Low cycle fatigue; Medium strength steel; Scanning electron microscopy; CRACK GROWTH; PLASTICITY; MECHANISM; FRACTURE; FAILURE;
D O I：
10.1002/adem.201700680
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The influence of hydrogen on low cycle fatigue (LCF) of 3.5NiCrMoV steel electrochemically hydrogen charged in the acidified pH 2 0.1M Na2SO4 solution is studied. In the presence of hydrogen, the fatigue life decreases significantly by approximate to 70 to approximate to 80% by: (i) the crack initiation period is decreased; and (ii) the crack growth rate is accelerated. SEM observation indicates that in the presence of hydrogen, the fracture surface shows flat transgranular fracture with vague striations and some intergranular fracture at lower stresses. The fatigue crack growth rate increases with increasing cyclic stress amplitude and with hydrogen fugacity. Once the fatigue crack reaches a critical length, the specimen becomes mechanical unstable and fracture due to ductile overload occurs. The hydrogen contribution to the final fracture process is not significant.
引用
收藏
页数：12
相关论文
共 50 条
  • [31] Influence of hydrogen on ultrahigh cycle fatigue properties of high strength spring steel 50CrV4
    Li Yongde
    Li Shouxin
    Yang Zhenguo
    Liu Yangbo
    Rong Lijian
    Hui Weijun
    Weng Yuqing
    [J]. ACTA METALLURGICA SINICA, 2008, 44 (01) : 64 - 68
  • [32] Influence of frequency on low cycle fatigue behavior of Pb-free solder 96.5Sn-3.5Ag
    Kanchanomai, C
    Miyashita, Y
    Mutoh, Y
    Mannan, SL
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 345 (1-2): : 90 - 98
  • [33] Low cycle fatigue behavior of a multiphase microalloyed medium carbon steel: comparison between ferrite-pearlite and quenched and tempered microstructures
    Sankaran, S
    Sarma, VS
    Padmanabhan, KA
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 345 (1-2): : 328 - 335
  • [34] Carbides and their influence on notched low cycle fatigue behavior of fine-grained IN718 gas turbine disk material
    Bhowal, Prabir R.
    Wusatowska-Sarnek, Agnieszka M.
    [J]. Superalloys 718, 625, 706 and Derivatives, Proceedings, 2005, : 341 - 349
  • [35] Masing Behavior and Microstructural Change of Quenched and Tempered High-Strength Steel Under Low Cycle Fatigue
    Bai, Feng-Mei
    Zhou, Hong-Wei
    Liu, Xiang-Hua
    Song, Meng
    Sun, Ya-Xin
    Yi, Hai-Long
    Huang, Zhen-Yi
    [J]. ACTA METALLURGICA SINICA-ENGLISH LETTERS, 2019, 32 (11) : 1346 - 1354
  • [36] Masing Behavior and Microstructural Change of Quenched and Tempered High-Strength Steel Under Low Cycle Fatigue
    Feng-Mei Bai
    Hong-Wei Zhou
    Xiang-Hua Liu
    Meng Song
    Ya-Xin Sun
    Hai-Long Yi
    Zhen-Yi Huang
    [J]. Acta Metallurgica Sinica (English Letters), 2019, 32 : 1346 - 1354
  • [37] Masing Behavior and Microstructural Change of Quenched and Tempered High-Strength Steel Under Low Cycle Fatigue
    Feng-Mei Bai
    Hong-Wei Zhou
    Xiang-Hua Liu
    Meng Song
    Ya-Xin Sun
    Hai-Long Yi
    Zhen-Yi Huang
    [J]. ActaMetallurgicaSinica(EnglishLetters), 2019, 32 (11) : 1346 - 1354
  • [38] Low-cycle fatigue mechanical behavior of 30CrMo steel under hydrogen environment and numerical verification of chaboche model
    Guan, Y. B.
    Wang, Q. Y.
    He, C.
    Fu, L.
    Lin, L.
    Zhang, Y. Q.
    Luo, Y. R.
    Wang, Z. G.
    Wu, X.
    [J]. MATERIALS RESEARCH EXPRESS, 2024, 11 (01)
  • [39] Hydrogen embrittlement behavior of high strength low carbon medium manganese steel under different heat treatments
    Du, Yu
    Gao, Xiuhua
    Lan, Liangyun
    Qi, Xiangyu
    Wu, Hongyan
    Du, Linxiu
    Misra, R. D. K.
    [J]. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2019, 44 (60) : 32292 - 32306
  • [40] Effect of Quench and Partitioning Treatment on Microstructure, Tensile Properties, and Low Cycle Fatigue Behavior of Low-Carbon High Strength Steel
    Arif, Sk Md.
    Bar, H. N.
    Sahoo, Biraj Kumar
    Chaudhary, Chandan
    Mandal, D.
    [J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2025,
12345