Electrical Properties of Epitaxial Thin Films of Oxyhydrides ATiO3-xHx (A = Ba and Sr)

We have studied electronic properties of perovskite oxyhydrides ATiO(3-x)H(x) (A = Ba, Sr). Epitaxial thin films of ATiO(3-x)H(x) with various hydride compositions, up to x = 0.58 for Ba and x = 0.45 for Sr, are prepared by the low-temperature CaH2 reduction of the corresponding oxide films deposited on (LaA-lO(3))(0.3)(SrAl0.5Ta0.5O3)O-3 (LSAT) substrates by pulsed laser deposition. Resistivity measurements for A = Sr show a metallic phase over a wide range of H- composition, implying a substantial stabilization of H is orbitals that should be distributed over O 2p orbitals. On the other hand, for A = Ba, a semiconducting behavior is seen up to 8% of H- substitution. Interestingly, a similar contrasting behavior is observed in a Nb-substituted BaTiO3 and SrTiO3, which suggests that a local cation off centering in lightly doped Ba films creates in-gap states in the band structure (as opposed to the Sr films), hindering the electron transport.