Microstructures and oxidation behavior of NiCrAlCoY-Al composite coatings on Ti-6Al-4V alloy substrate via high-energy mechanical alloying method

被引：28

作者：

Li, Yifeng ^{[1
]}

Chen, Cheng ^{[1
]}

Han, Tengfei ^{[1
]}

Ranabhat, Jwala ^{[1
]}

Feng, Xiaomei ^{[1
]}

Shen, Yifu ^{[1
]}

机构：

[1] Nanjing Univ Aeronaut & Astronaut, Coll Mat Sci & Technol, 29 Jiangjun Rd, Nanjing 210016, Jiangsu, Peoples R China

来源：

JOURNAL OF ALLOYS AND COMPOUNDS | 2017年 / 697卷

基金：

中国国家自然科学基金;

关键词：

NiCrAlCoY-Al; Mechanical alloying; Gradient composite coating; Microstructures; High-temperature oxidation resistance; THERMAL BARRIER COATINGS; CR; IMPROVEMENT; DEPOSITION; RESISTANCE; EVOLUTION; CORROSION;

D O I：

10.1016/j.jallcom.2016.10.171

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

In the present work, NiCrAlCoY-Al gradient composite coatings were successfully fabricated on Ti-6Al-4V alloy substrate via high-energy mechanical alloying method. The microstructures and elemental and phase composition of the coatings have been studied. Effects of both NiCrAlCoY-Al powder ratio and milling time on the fabrication of composite coating were investigated. The NiCrAlCoY-Al weight ratio 65: 35 was considered the optimal powder ratio to fabricate the coating at the selected milling parameters. The high-temperature cyclic oxidation tests were performed at 850 degrees C and 750 degrees C. The fabricated sample using 65: 35 wt ratio and 4 h milling time showed the best oxidation resistance due to the low mass gain, rutile TiO2 undetected surface, and densified composite cross-section morphology. The decreased oxygen content of the oxidized cross-section line scanning results revealed the improvement of oxidation resistance. The oxidation process of the as-fabricated coating had been divided into five steps. Three protective Al2O3 oxide layers together with other alloy compounds could prevent the further diffusion of oxygen. The coating could enhance the oxidation resistance of the substrate. (C) 2016 Elsevier B. V. All rights reserved.

引用

页码：268 / 281

页数：14

共 27 条

[1] Creep behavior of Pt-aluminide (PtAl) coated directionally solidified Ni-based superalloy CM-247LC after thermal exposure [J].

Alam, Md. Zafir ;

Satyanarayana, D. V. V. ;

Chatterjee, D. ;

Sarkar, R. ;

Das, D. K. .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2015, 641 :84-95

[2]

Birks N, 2010, Introduction to the high temperature oxidation of metals

[3] Surface characterization and mechanical property evaluation of thermally oxidized Ti-6Al-4V [J].

Biswas, Amit ;

Majumdar, Jyotsna Dutta .

MATERIALS CHARACTERIZATION, 2009, 60 (06) :513-518

[4] Investigation of Cr-Al composite coatings fabricated on pure Ti substrate via mechanical alloying method: Effects of Cr-Al ratio and milling time on coating, and oxidation behavior of coating [J].

Chen, Cheng ;

Zhang, Jiaping ;

Duan, Cuiyuan ;

Feng, Xiaomei ;

Shen, Yifu .

JOURNAL OF ALLOYS AND COMPOUNDS, 2016, 660 :208-219

[5] The effect of SMAT-induced grain refinement and dislocations on the corrosion behavior of Ti-25Nb-3Mo-3Zr-2Sn alloy [J].

Huang, Run ;

Han, Yong .

MATERIALS SCIENCE & ENGINEERING C-MATERIALS FOR BIOLOGICAL APPLICATIONS, 2013, 33 (04) :2353-2359

[6]

Leyens Christoph., 2006, Titanium and Titanium Alloys: Fundamentals and Applications

[7] Preparation of Ti-Cr and Ti-Cu flame-retardant coatings on Ti-6Al-4V using a high-energy mechanical alloying method: A preliminary research [J].

Li, Bo ;

Ding, Rundong ;

Shen, Yifu ;

Hu, Yongzhi ;

Guo, Yan .

MATERIALS & DESIGN, 2012, 35 :25-36

[8] Thermal fatigue behavior of thermal barrier coatings with the MCrAlY bond coats by cold spraying and low-pressure plasma spraying [J].

Li, Yong ;

Li, Chang-Jiu ;

Yang, Guan-Jun ;

Xing, Lu-Kuo .

SURFACE & COATINGS TECHNOLOGY, 2010, 205 (07) :2225-2233

[9] Microstructure evolution of Cr coatings on Cu substrates prepared by mechanical alloying method [J].

Li, Yongcan ;

Chen, Cheng ;

Deng, Ruixiang ;

Feng, Xiaomei ;

Shen, Yifu .

POWDER TECHNOLOGY, 2014, 268 :165-172

[10] Characterization and oxidation behavior of NiCoCrAlY coating fabricated by electrophoretic deposition and vacuum heat treatment [J].

Li, Zhiming ;

Qian, Shiqiang ;

Wang, Wei .

APPLIED SURFACE SCIENCE, 2011, 257 (10) :4616-4620

← 1 2 3 →