Effect of fatigue loading on impact damage and buckling/post-buckling behaviors of stiffened composite panels under axial compression

被引：23
作者：
Feng, Yu [1 ]
He, Yuting [1 ]
Zhang, Haoyu [1 ]
Tan, Xiangfei [1 ]
An, Tao [1 ]
Zheng, Jie [2 ]
机构：
[1] Air Force Engn Univ, Aeronaut & Astronaut Engn Coll, Xian 710038, Peoples R China
[2] Aviat Ind Corp, Aircraft Inst 1, Xian 710089, Peoples R China
来源：
COMPOSITE STRUCTURES | 2017年 / 164卷
基金：
中国国家自然科学基金;
关键词：
Stiffened composite panels; Impact; Fatigue loading; Buckling; Post-buckling; LOW-VELOCITY IMPACT; POSTBUCKLING BEHAVIOR; CURVED PANELS; SIMULATION; PREDICTION; DESIGN;
D O I：
10.1016/j.compstruct.2016.12.069
中图分类号：
O3 [力学];
学科分类号：
08 ; 0801 ;
摘要：
Effect of fatigue loading on impact damage and buckling/post-buckling behaviors of stiffened composite panels under axial compression were studied in this paper. Barely visible impact damage (BVID) was introduced to stiffened composite panels. Damage areas and crater depths data were analyzed and their distributions were determined, whose upper limits were also calculated under different reliability. Then fatigue experiments were conducted on impact specimens. Damage areas, damage site shapes and crater depths were measured at every certain fatigue cycles. Compression after impact (CAI) as well as compression after impact and fatigue (CALF) were also studied, with a comparison of virgin specimens. The results exhibited impact damage and the following fatigue loading had no obvious influence on the bucking load and buckling modes. Additionally, failure modes of all types of specimens were similar, which included debonding and fracture of stiffeners together with splitting and cracking of skin bays. However, the average failure load of impact specimens decreased 9.9% compared to that of virgin specimens. Fatigue loading would lead a further decrease about 6.1% in failure load compared to impact specimens, although the impact damage had no obvious changes during and after fatigue loading. (C) 2016 Elsevier Ltd. All rights reserved.
引用
收藏
页码：248 / 262
页数：15
相关论文
共 37 条
[11]   Damage prediction in composite sandwich panels subjected to low-velocity impact [J].
Feng, D. ;
Aymerich, F. .
COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2013, 52 :12-22
[12]  
Feng Y, POLYM COMPOS
[13]   Investigation on tension-tension fatigue performances and reliability fatigue life of T700/MTM46 composite laminates [J].
Feng, Yu ;
Gao, Chao ;
He, Yuting ;
An, Tao ;
Fan, Chaohua ;
Zhang, Haoyu .
COMPOSITE STRUCTURES, 2016, 136 :64-74
[14]   Effect of hygrothermal condition on buckling and post-buckling performance of CCF300/5228A aero composite stiffened panel under axial compression [J].
Feng, Yu ;
He, Yuting ;
An, Tao ;
Cui, Ronghong ;
Shao, Qing ;
Fan, Chaohua .
JOURNAL OF REINFORCED PLASTICS AND COMPOSITES, 2015, 34 (12) :989-999
[15]   DAMAGE MECHANISM CHARACTERIZATION IN COMPOSITE DAMAGE TOLERANCE INVESTIGATIONS [J].
HULL, D ;
SHI, YB .
COMPOSITE STRUCTURES, 1993, 23 (02) :99-120
[16]   Evaluation for residual strength and fatigue characteristics after impact in CFRP composites [J].
Koo, Jae-Mean ;
Choi, Jung-Hun ;
Seok, Chang-Sung .
COMPOSITE STRUCTURES, 2013, 105 :58-65
[17]   Effect of back pressure on impact and compression-after-impact characteristics of composites [J].
Kulkarni, Mandar D. ;
Goel, Rahul ;
Naik, N. K. .
COMPOSITE STRUCTURES, 2011, 93 (02) :944-951
[18]   Investigations on Buckling Behaviour of Laminated Curved Composite Stiffened Panels [J].
Kumar, N. Jeevan ;
Babu, P. Ramesh ;
Pandu, Ratnakar .
APPLIED COMPOSITE MATERIALS, 2014, 21 (02) :359-376
[19]   Experimental investigation on edge impact damage and Compression After-Impact (CAI) behavior of stiffened composite panels [J].
Li, N. ;
Chen, P. H. .
COMPOSITE STRUCTURES, 2016, 138 :134-150
[20]   Simulation of low velocity impact on composite laminates with progressive failure analysis [J].
Maio, L. ;
Monaco, E. ;
Ricci, F. ;
Lecce, L. .
COMPOSITE STRUCTURES, 2013, 103 :75-85
1234