Fatigue Behavior of Blast-treated Out-of-plane Gusset Fillet Welded Joints

被引：0
作者：
Kim, In-Tae [1 ]
Nhan, Le Van Phuoc [2 ]
Lee, Dong-Uk [2 ]
机构：
[1] Pusan Natl Univ, Dept Civil Engn, Pusan 609735, South Korea
[2] Pukyong Natl Univ, Dept Civil & Construct Engn, Pusan 608739, South Korea
来源：
INTERNATIONAL JOURNAL OF STEEL STRUCTURES | 2008年 / 8卷 / 03期
关键词：
steel structure; fatigue; welded joint; fatigue life; blast cleaning; out-of-plane gusset joint;
D O I：
暂无
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
Blast cleaning prior to coating has been applied in newly built steel structures for cleaning forged surface and increasing adhesive property of applied coating systems. However, the effect of surface preparations by blast cleaning treatment on fatigue behavior of welded joints is not considered in Fatigue Design Codes. In this paper, fatigue tests were carried out on four types of out-of-plane gusset fillet welded joints, as-welded gusset specimens and three types of blast-treated gusset specimens, and then the effect of the blast cleaning treatment on the fatigue behavior of the welded joints was studied. The radius of curvature at weld toe of the blast-treated specimens was larger than that of as-welded specimens. The fatigue test results showed that the fatigue life of the blast-treated specimens is longer than that of as-welded specimens in low stress ranges, even though there is no significant difference in fatigue life between the two types in high stress ranges. Over 167% increase in fatigue limit could be realized by using blast cleaning treatment.
引用
收藏
页码：155 / 161
页数：7
相关论文
共 50 条
[31]   Out-of-plane singular stress fields in V-notched plates and welded lap joints induced by in-plane shear load conditions [J].
Berto, F. ;
Lazzarin, P. ;
Kotousov, A. ;
Harding, S. .
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2011, 34 (04) :291-304
[32]   Estimating the fatigue behavior of welded joints in the VHCF regime [J].
Krasovskyy, A. ;
Bachmann, D. .
INTERNATIONAL JOURNAL OF STRUCTURAL INTEGRITY, 2012, 3 (04) :326-343
[33]   Experimental and numerical investigation on fatigue performance of non-load-carrying fillet welded joints [J].
Zong, Liang ;
Shi, Gang ;
Wang, Yuan-Qing ;
Li, Zhong-Xian ;
Ding, Yang .
JOURNAL OF CONSTRUCTIONAL STEEL RESEARCH, 2017, 130 :193-201
[34]   Residual and assembling stress analyses on fillet welded joints of flange pipes and the fatigue strength prediction [J].
Oh, Gyoko ;
Akiniwa, Yoshiaki .
THIN-WALLED STRUCTURES, 2019, 136 :138-149
[35]   Fatigue life of welded joints according to energy criteria in the critical plane [J].
T. Lagoda .
Strength of Materials, 2006, 38 (4) :417-422
[36]   Influence of the atmosphere corrosion on the fatigue life of welded T-joints treated by high frequency mechanical impact [J].
Knysh, Vitalii ;
Solovei, Sergii ;
Nyrkova, Lyudmila ;
Klochkov, Illya ;
Motrunich, Sviatoslav .
6TH INTERNATIONAL CONFERENCE FRACTURE MECHANICS OF MATERIALS AND STRUCTURAL INTEGRITY (FMSI 2019), 2019, 16 :73-80
[37]   Fatigue of out-of-plane fibre waviness defects: experimental and numerical study [J].
Mukhopadhyay, Supratik ;
Hallett, Stephen R. .
20TH INTERNATIONAL CONFERENCE ON COMPOSITE MATERIALS, 2015,
[38]   Numerical simulations of fatigue crack initiation and propagation based on re-tensile plastic zone generating load criterion for in-plane gusset welded joints [J].
Yukinobu Nagata ;
Koji Gotoh ;
Masahiro Toyosada .
Journal of Marine Science and Technology, 2009, 14 :104-114
[39]   FATIGUE BEHAVIOR AND DAMAGE MONITORING OF ULTRASONIC WELDED HYBRID JOINTS [J].
Huxhold, Stefan ;
Balle, Frank ;
Wagner, Guntram ;
Eifler, Dietmar .
PROCEEDINGS OF THE 13TH INTERNATIONAL CONFERENCE ON ALUMINUM ALLOYS (ICAA13), 2012, :505-510
[40]   Fatigue Behavior of Electron Beam Welded Dissimilar Metal Joints [J].
Calik, A. ;
Karakas, M. S. ;
Varol, R. .
WELDING JOURNAL, 2012, 91 (02) :50S-52S
12345