Epitaxial growth of γ-(AlxGa1-x)2O3 alloy thin films on spinel substrates via mist chemical vapor deposition

Among the five polymorphs of alpha, beta, gamma, delta, and kappa(epsilon)-gallium oxide (Ga2O3), we focused on metastable cubic gamma-Ga2O3, which exhibits a defect spinel structure, from the viewpoint of lattice matching. Alloying gamma-Ga2O3 with y-aluminum oxide (gamma-Ga2O3), which exhibits the same crystal structure as that of the former, is effective for lattice-matched growth on a spinel substrate as well as band gap engineering. At the composition ratio x = 0.48, gamma-aluminum gallium oxide (gamma-(AlxGa1-x)(2)O-3) lattice matched to the spinel substrate, and its band gap energy increased to 5.88 eV. Thus, gamma-(AlxGa1-x)(2)O-3 is a promising material for wide band gap semiconductors that are lattice matched to the substrates, for applications in powerswitching devices and deep-ultraviolet optoelectronics. In this study, we demonstrated the epitaxial growth of gamma-(AlxGa1-x)(2)O-3 alloy thin films on spinel substrates using mist chemical vapor deposition. At the Al concentration of 0.11 M, the epitaxial gamma-(AlxGa1-x)(2)O-3 thin film was successfully grown with Laueoscillations observed in the X-ray diffraction 2 theta-omega scan. Moreover, transmission electron microscopy measurements revealed that the gamma-(AlxGa1-x)(2)O-3 thin film was lattice matched and grown on the spinel substrate with few misfit dislocations at the interface. Band gap engineering was achieved in the range of 5.0-6.0 eV by estimating the direct band gap energy. Thus, our results, which indicate the possibility of limited dislocations due to lattice matches, are expected to facilitate the development of materials with wider band gaps based on gamma-(AlxGa1-x)(2)O-3. (C) 2020 Elsevier B.V. All rights reserved.