Stable acrylate/triethoxyvinylsilane (VTES) core-shell emulsion with low surface tension made by modified micro-emulsion polymerization: Effect of different mass ratio of MMA/BA in the core and shell

被引：20
作者：
Zhang, Yun-fei [1 ,2 ]
Zhang, Rui [1 ,2 ]
Yang, Chao-long [1 ,2 ]
Xu, Jing [1 ,2 ]
Zheng, Jian [1 ,2 ]
Lu, Man-geng [1 ]
机构：
[1] Chinese Acad Sci, Guangzhou Inst Chem, Guangzhou 510650, Guangdong, Peoples R China
[2] Univ Chinese Acad Sci, Beijing 100039, Peoples R China
来源：
COLLOIDS AND SURFACES A-PHYSICOCHEMICAL AND ENGINEERING ASPECTS | 2013年 / 436卷
关键词：
Stable core-shell latex; Emulsion polymerization; Surface tension; Mass ratio of MMA/BA; FLUOROACRYLATE COPOLYMER LATEXES; BUTYL ACRYLATE; MINIEMULSION COPOLYMERIZATION; NANOCOMPOSITE EMULSION; POLYACRYLATE LATEX; VINYL-ACETATE; PARTICLES; SILICONE; SILOXANE; FILM;
D O I：
10.1016/j.colsurfa.2013.07.028
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
Stable acrylate/triethoxyvinylsilane (VTES) core shell emulsion with different mass ratio of MMA/BA in the core and shell was prepared via a modified micro-emulsion polymerization process. The chemical composition and core shell structure were investigated by Fourier transform infrared (FTIR) spectrometry, differential scanning calorimetry (DSC) and transmission electron microscopy (TEM), respectively. Effect of MMA/BA mass ratio in the core and shell on the film-forming ability, surface tension of latex was also studied. Finally, water absorption and thermal stability of the latex films were characterized. It was found that the surface tension of emulsion can be reduced to 32.9 N/m when the MMA/BA mass ratio in the shell is 6/4. The water absorption of the latex film could be improved at a proper mass ratio of MMA/BA in core and shell, but adjusting the mass ratio of MMA/BA in the shell has little influence on the thermal stability of latex film. This work provides a method of preparing environment-friendly latex with low surface tension and excellent water resistance for coating applications by regulating the mass ratio of monomers in a modified micro-emulsion polymerization process. (C) 2013 Elsevier B.V. All rights reserved.
引用
收藏
页码：549 / 556
页数：8
相关论文
共 35 条
[1]   Polyurethane macromers - new building blocks for acrylic hybrid emulsions with outstanding performance [J].
Adler, HJ ;
Jahny, K ;
Vogt-Birnbrich, B .
PROGRESS IN ORGANIC COATINGS, 2001, 43 (04) :251-257
[2]   Synthesis and characterization of water-based poly(vinyl acetate-co-butyl acrylate) latexes containing oligomeric protective colloid [J].
Berber, Hale ;
Sarac, Ayfer ;
Yildirim, Huseyin .
POLYMER BULLETIN, 2011, 66 (07) :881-892
[3]   Miniemulsion copolymerization of methyl methacrylate and butyl acrylate by ultrasonic initiation [J].
Bradley, MA ;
Prescott, SW ;
Schoonbrood, HAS ;
Landfester, K ;
Grieser, F .
MACROMOLECULES, 2005, 38 (15) :6346-6351
[4]  
Cao TY, 2007, SYNTHESIS PRINCIPLE, P618
[5]   Preparation and properties of polytetrafluoroethylene-modified polyacrylate via emulsion polymerization [J].
Chen, ZX ;
Li, JF ;
Cui, XJ ;
Cheng, XL ;
Wang, HY .
COLLOID AND POLYMER SCIENCE, 2005, 284 (02) :218-223
[6]   Synthesis and characterization of core-shell LIPN-fluorine-containing polyacrylate latex [J].
Cheng, Xiuli ;
Chen, Zhengxia ;
Shi, Tongshun ;
Wang, Hongyan .
COLLOIDS AND SURFACES A-PHYSICOCHEMICAL AND ENGINEERING ASPECTS, 2007, 292 (2-3) :119-124
[7]   Emulsifier-free core-shell polyacrylate latex nanoparticles containing fluorine and silicon in shell [J].
Cui, Xuejun ;
Zhong, Shuangling ;
Wang, Hongyan .
POLYMER, 2007, 48 (25) :7241-7248
[8]   Synthesis and surface properties of PDMS-acrylate emulsion with gemini surfactant as co-emulsifier [J].
Deng, Xiaobo ;
Luo, Rong ;
Chen, Hualin ;
Liu, Bailing ;
Feng, Yujun ;
Sun, Yuhai .
COLLOID AND POLYMER SCIENCE, 2007, 285 (08) :923-930
[9]   Preparation and properties of poly(silicone-co-acrylate)/montmorillonite nanocomposite emulsion [J].
Feng, Xiaoping ;
Zhong, Anyong ;
Chen, Deben .
JOURNAL OF APPLIED POLYMER SCIENCE, 2006, 101 (06) :3963-3970
[10]   Preparation and properties of core [poly(styrene-n-butyl acrylate)]-shell [poly(styrene-methyl methacrylate-vinyl triethoxide silane)] structured latex particles with self-crosslinking characteristics [J].
Guo, TY ;
Chen, X ;
Song, MD ;
Zhang, BH .
JOURNAL OF APPLIED POLYMER SCIENCE, 2006, 100 (03) :1824-1830
1234