Study on soap-free P(MMA-EA-AA or MAA) latex particles with narrow size distribution

Soap-free poly(methyl methacrylate-ethyl acrylate-acrylic acid or methacrylic acid) MMMA-EA-AA or MAM particles with narrow size distribution were synthesized by seeded emulsion polymerization of methyl methacrylate (MMA), ethyl acrylate (EA) and acrylic acid (AA) or methacrylic acid (MAA), and the influences of the mass ratio of core/shell monomers used in the two stages of polymerization ([C/S](w)) and initiator amount on polymerization, particle size and its distribution were investigated by using different monomer addition modes. Results showed that when the batch swelling method was used, the monomer conversion was more than 96.0% and particle size distribution was narrow, and the particle size increased first and then remained almost unchanged at around 600nm with the [C/S](w) decreased. When the drop-wise addition method was used, the monomer conversion decreased slightly with [C/S](w) decreased, and large particles more than 750 nm in diameter can be obtained; with the initiator amount increased, the particle size decreased and the monomer conversion had a trend to increase; the particle size distribution was broader and the number of new particles was more in the AA system than in the MAA system; but the AA system was more stable than the MAA system at both low and high initiator amount. Copyright (c) 2006 John Wiley & Sons, Ltd.