Scratch testing of WC/Co hardmetals

被引：37

作者：

Zunega, J. C. P. ^{[1
]}

Gee, M. G.

Wood, R. J. K. ^{[1
]}

Walker, J. ^{[1
]}

机构：

[1] Univ Southampton, Natl Ctr Adv Tribol Southampton nCATS, Southampton SO9 5NH, Hants, England

来源：

TRIBOLOGY INTERNATIONAL | 2012年 / 54卷

基金：

英国工程与自然科学研究理事会;

关键词：

WC/Co hardmetals; Tribo-layer; Wear; Coefficient of friction; WC-CO HARDMETALS; SLIDING CONTACT; HARD METALS; ABRASION; MECHANISMS; WEAR;

D O I：

10.1016/j.triboint.2012.02.027

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

Two grades of WC/Co hardmetals, a fine-grained sample and coarse-grained sample, were tested using single and multiple scratch tests with a spherical diamond stylus. The variation in damage mechanism with increasing number of scratch repeats was analysed using SEM, FIB and 3D confocal microscopy. An interesting feature is the formation of a thin tribo-layer on the surface of the scratched region, which becomes more evident at increased scratch repeats. Variations in the coefficient of friction were attributed to changes in the topography of the stylus and formation of a tribo-layer on the scratched surface. Crown Copyright (C) 2012 Published by Elsevier Ltd. All rights reserved.

引用

页码：77 / 86

页数：10

共 50 条

[21] Oxidation-induced strength degradation of WC-Co hardmetals
Casas, B
Ramis, X
Anglada, M
Salla, JM
Llanes, L
INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2001, 19 (4-6) : 303 - 309
[22] Interlaboratory Measurements of Contiguity in WC-Co Hardmetals
Mingard, Ken P.
Roebuck, Bryan
METALS, 2019, 9 (03):
[23] Grain boundaries in WC-Co hardmetals with facetted and rounded WC grains
Zaitsev, A. A.
Sidorenko, D.
Konyashin, I
MATERIALS LETTERS, 2022, 306
[24] EBSD evaluation of damage in micro-tribology experiments on WC/Co hardmetals
Gee, M. G.
Mingard, K.
Nunn, J. W.
WEAR, 2023, 524
[25] Dependence of microscale abrasion mechanisms of WC-Co hardmetals on abrasive type
Shipway, PH
Hogg, JJ
WEAR, 2005, 259 (1-6) : 44 - 51
[26] Some analytical consequences of experimental data on properties of WC-Co hardmetals
Golovchan, V. T.
INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2008, 26 (04) : 301 - 305
[27] Fracture behaviour of WC-Co hardmetals with WC partially substituted by titanium carbide
Szutkowska, M.
Boniecki, M.
Cygan, S.
Kalinka, A.
Grilli, M. L.
Balos, S.
E-MRS FALL SYMPOSIUM I: SOLUTIONS FOR CRITICAL RAW MATERIALS UNDER EXTREME CONDITIONS, 2018, 329
[28] Comparison of the friction and wear behaviour of WC-Ni-Co-Cr and WC-Co hardmetals in contact with steel at high temperatures
Aristizabal, M.
Ardila, L. C.
Veiga, F.
Arizmendi, M.
Fernandez, J.
Sanchez, J. M.
WEAR, 2012, 280 : 15 - 21
[29] Application of EBSD to the evaluation of plastic deformation in the mechanical testing of WC/Co hardmetal
Gee, Mark
Mingard, Ken
Roebuck, Bryan
INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2009, 27 (02) : 300 - 312
[30] Densification, mechanical properties and wear behavior of WC-VC-Co-Al hardmetals
Arenas, FJ
Matos, A
Cabezas, M
Di Rauso, C
Grigorescu, C
INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2001, 19 (4-6) : 381 - 387

← 1 2 3 4 5 →