The high-temperature tribological properties of Si-DLC films

被引：43

作者：

Yang, Baoping ^{[2
]}

Zheng, Yu ^{[1
,2
]}

Zhang, Bin ^{[1
]}

Wei, Li ^{[1
]}

Zhang, Junyan ^{[1
]}

机构：

[1] Chinese Acad Sci, Lanzhou Inst Chem Phys, State Key Lab Solid Lubricat, Lanzhou 730000, Peoples R China

[2] Lanzhou Univ Technol, Dept Petrochem Technol, Lanzhou 730050, Peoples R China

来源：

SURFACE AND INTERFACE ANALYSIS | 2012年 / 44卷 / 13期

关键词：

silicon-containing diamond-like-carbon films; high-temperature tribology; thermal stability; AMORPHOUS-CARBON; THERMAL-STABILITY; BEHAVIOR; COATINGS;

D O I：

10.1002/sia.5094

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

The tribological properties of Silicon-containing diamond-like-carbon (Si-DLC) films, deposited by magnetron sputtering Si target in methane/argon atmosphere, were studied in comparison with diamond-like-carbon (DLC) films. The DLC films disappeared because of the oxidation in the air at 500 degrees C, whereas the Si-DLC films still remained, implying that the addition of Si improved significantly the thermal stability of DLC films. Retarded hydrogen release from DLC film at high temperature and silicon oxide on the surface might have contributed to lower friction coefficient of the Si-DLC films both after annealing treatment and in situ high-temperature environment. Copyright (C) 2012 John Wiley & Sons, Ltd.

引用

页码：1601 / 1605

页数：5

共 19 条

[1] High temperature tribological behavior of W-DLC against aluminum [J].

Abou Gharam, A. ;

Lukitsch, M. J. ;

Balogh, M. P. ;

Irish, N. ;

Alpas, A. T. .

SURFACE & COATINGS TECHNOLOGY, 2011, 206 (07) :1905-1912

[2] High temperature tribological behaviour of carbon based (B4C and DLC) coatings in sliding contact with aluminum [J].

Abou Gharam, A. ;

Lukitsch, M. J. ;

Balogh, M. P. ;

Alpas, A. T. .

THIN SOLID FILMS, 2010, 519 (05) :1611-1617

[3] Improved high-temperature stability of Si incorporated a-C:H films [J].

Camargo, SS ;

Neto, ALB ;

Santos, RA ;

Freire, FL ;

Carius, R ;

Finger, F .

[4] Thermal stability of Cr-doped diamond-like carbon films synthesized by cathodic arc evaporation [J].

Chiu, MC ;

Hsieh, WP ;

Ho, WY ;

Wang, DY ;

Shieu, FS .

THIN SOLID FILMS, 2005, 476 (02) :258-263

[5] The effects of Si incorporation on the thermal and tribological properties of DLC films deposited by PBII&D with bipolar pulses [J].

Choi, J. ;

Nakao, S. ;

Miyagawa, S. ;

Ikeyama, M. ;

Miyagawa, Y. .

SURFACE & COATINGS TECHNOLOGY, 2007, 201 (19-20) :8357-8361

[6] USE OF RAMAN-SCATTERING TO INVESTIGATE DISORDER AND CRYSTALLITE FORMATION IN AS-DEPOSITED AND ANNEALED CARBON-FILMS [J].

DILLON, RO ;

WOOLLAM, JA ;

KATKANANT, V .

PHYSICAL REVIEW B, 1984, 29 (06) :3482-3489

[7] Interpretation of Raman spectra of disordered and amorphous carbon [J].

Ferrari, AC ;

Robertson, J .

PHYSICAL REVIEW B, 2000, 61 (20) :14095-14107

[8] Temperature dependent properties of silicon containing diamondlike carbon films prepared by plasma source ion implantation [J].

Hatada, R. ;

Flege, S. ;

Baba, K. ;

Ensinger, W. ;

Kleebe, H. -J. ;

Sethmann, I. ;

Lauterbach, S. .

JOURNAL OF APPLIED PHYSICS, 2010, 107 (08)

[9] SYMMETRY-BREAKING IN NITROGEN-DOPED AMORPHOUS-CARBON - INFRARED OBSERVATION OF THE RAMAN-ACTIVE G-BANDS AND D-BANDS [J].

KAUFMAN, JH ;

METIN, S ;

SAPERSTEIN, DD .

PHYSICAL REVIEW B, 1989, 39 (18) :13053-13060

[10] Elevated temperature tribological behavior of non-hydrogenated diamond-like carbon coatings against 319 aluminum alloy [J].

Konca, E ;

Cheng, YT ;

Weiner, AM ;

Dasch, JM ;

Alpas, A .

SURFACE & COATINGS TECHNOLOGY, 2006, 200 (12-13) :3996-4005

← 1 2 →