Change in Wear Behaviour of Ti and Ti6Al4V after Plasma Immersion Ion Implantation

被引：5
|
作者：
Ducherow, Marlen [1 ]
Fleischer, Alexander [1 ]
Maendl, Stephan [1 ]
机构：
[1] Leibniz Inst Oberflachenmodifizierung, D-04318 Leipzig, Germany
来源：
PLASMA PROCESSES AND POLYMERS | 2007年 / 4卷
关键词：
diffusion; PIII; titanium; wear;
D O I：
10.1002/ppap.200731414
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
The influence of the layer thickness and the microstructure of Ti and Ti6Al4V treated with oxygen plasma immersion ion implantation (PIII) on the respective wear rates are investigated. The implantation temperature was varied from 250 up to 550 degrees C at fluences between 6 and 18 x 10 17 at. . cm(-2). The wear tests were performed in a rotating ball-on-disc tribometer with an alumina ball. No difference in the wear rate was observed between Ti and Ti6AlV at higher temperatures, while significant differences were presented at lower temperatures, which were not solely correlated with the layer thickness.
引用
收藏
页码：S602 / S606
页数：5
相关论文
共 50 条
  • [31] Wear properties of nonhydrogenated, hydrogenated, and dehydrogenated Ti6Al4V alloy
    Yuan, Bao-Guo
    Yu, Hai-Ping
    Li, Chun-Feng
    Sun, Dong-Li
    RARE METALS, 2018, 37 (07) : 574 - 578
  • [32] Use of nitrogen ion implantation for modification of the tribological properties of titanium alloy Ti6Al4V
    Kaminski, M.
    Budzynski, P.
    Wiertel, M.
    Drozdziel, A.
    INTERNATIONAL AUTOMOTIVE CONFERENCE (KONMOT2018), 2018, 421
  • [33] Plasma nitriding behavior of Ti6Al4V orthopedic alloy
    Yildiz, F.
    Yetim, A. F.
    Alsaran, A.
    Celik, A.
    SURFACE & COATINGS TECHNOLOGY, 2008, 202 (11): : 2471 - 2476
  • [34] Surface Modification of Ti6Al4V Alloy by Silver and Tantalum Dual-Ion Implantation
    Leng Chongyan
    Zhou Rong
    Zhang Xu
    RARE METAL MATERIALS AND ENGINEERING, 2013, 42 (07) : 1367 - 1371
  • [35] Characteristics and wear performance of bonded Ti6Al4V alloy prepared by double glow plasma surface alloying
    Qin, Lin
    Liu, Chengsong
    Yang, Kunkun
    Tang, Bin
    SURFACE & COATINGS TECHNOLOGY, 2013, 225 : 92 - 96
  • [36] Study on Wear and Corrosion Properties of Ti6Al4V Alloy by Laser Gas Nitriding
    Zhang Chunhua
    Tang Liwen
    Hu Fang
    Zhang Song
    Man Hauchung
    MATERIALS AND MANUFACTURING, PTS 1 AND 2, 2011, 299-300 : 188 - +
  • [37] The Effect of Coatings on the Wear Behavior of Ti6Al4V Alloy Used in Biomedical Applications
    Danisman, S.
    Odabas, D.
    Teber, M.
    9TH INTERNATIONAL CONFERENCE ON TRIBOLOGY (BALKANTRIB'17), 2018, 295
  • [38] Microstructure, mechanical and wear properties of laser surface melted Ti6Al4V alloy
    Balla, Vamsi Krishna
    Soderlind, Julie
    Bose, Susmita
    Bandyopadhyay, Amit
    JOURNAL OF THE MECHANICAL BEHAVIOR OF BIOMEDICAL MATERIALS, 2014, 32 : 335 - 344
  • [39] Dry Sliding Wear Behaviour of Shot Peened TI6AL4V Alloys at Different Peening Times
    Avcu, Y. Yildiran
    Yetik, O.
    Kocoglu, H.
    Avcu, E.
    Sinmazcelik, T.
    ACTA PHYSICA POLONICA A, 2018, 134 (01) : 349 - 353
  • [40] Influence of Interstitial Oxygen on the Tribology of Ti6Al4V
    Kuemmel, Daniel
    Schneider, Johannes
    Gumbsch, Peter
    TRIBOLOGY LETTERS, 2020, 68 (03)
12345