Change in Wear Behaviour of Ti and Ti6Al4V after Plasma Immersion Ion Implantation

被引：5
|
作者：
Ducherow, Marlen [1 ]
Fleischer, Alexander [1 ]
Maendl, Stephan [1 ]
机构：
[1] Leibniz Inst Oberflachenmodifizierung, D-04318 Leipzig, Germany
来源：
PLASMA PROCESSES AND POLYMERS | 2007年 / 4卷
关键词：
diffusion; PIII; titanium; wear;
D O I：
10.1002/ppap.200731414
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
The influence of the layer thickness and the microstructure of Ti and Ti6Al4V treated with oxygen plasma immersion ion implantation (PIII) on the respective wear rates are investigated. The implantation temperature was varied from 250 up to 550 degrees C at fluences between 6 and 18 x 10 17 at. . cm(-2). The wear tests were performed in a rotating ball-on-disc tribometer with an alumina ball. No difference in the wear rate was observed between Ti and Ti6AlV at higher temperatures, while significant differences were presented at lower temperatures, which were not solely correlated with the layer thickness.
引用
收藏
页码：S602 / S606
页数：5
相关论文
共 50 条
  • [1] Wear resistance of plasma immersion ion implanted Ti6Al4V
    Johns, SM
    Bell, T
    Samandi, M
    Collins, GA
    SURFACE & COATINGS TECHNOLOGY, 1996, 85 (1-2): : 7 - 14
  • [2] Effect of plasma immersion ion implantation on wear behavior of Ti-6Al-4V alloy
    Resende, Fabricia Assis
    Silva, Maria Margareth
    Oliveira, Rogerio de Moares
    Silva, Carla
    Pichon, Luc
    Radi, Polyana Alves
    dos Reis, Adriano Goncalves
    Reis, Danieli Aparecida Pereira
    SURFACE TOPOGRAPHY-METROLOGY AND PROPERTIES, 2023, 11 (01)
  • [3] Wear behaviour of nitric acid passivated cp Ti and Ti6Al4V
    Masmoudi, M.
    Assoul, M.
    Wery, M.
    Abdelhedi, R.
    El Halouani, F.
    Monteil, G.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 478 (1-2) : 726 - 730
  • [4] Characterization of Ti-6Al-4V modified by nitrogen plasma immersion ion implantation
    Alonso, F
    Rinner, M
    Loinaz, A
    Onate, JI
    Ensinger, W
    Rauschenbach, B
    SURFACE & COATINGS TECHNOLOGY, 1997, 93 (2-3): : 305 - 308
  • [5] Characteristics and Wear Performance of Nitrided Ti6Al4V
    Siyahjani, Farid
    Cimenoglub, Huseyin
    DIFFUSION IN SOLIDS AND LIQUIDS VII, 2012, 326-328 : 494 - 497
  • [6] Modification of Ti6Al4V Corrosion Property by Nitrogen Ion Implantation
    Shokouhy, Ali
    Ghoraneviss, Mahmood
    Larijani, Majid M.
    Yari, Mehdi
    Hosseini, S. H. Haji
    Eshghabadi, Majid
    JOURNAL OF FUSION ENERGY, 2011, 30 (05) : 437 - 441
  • [7] Improvements of the surface properties of Ti6Al4V by plasma based ion implantation at high temperatures
    Silva, G.
    Ueda, M.
    Otani, C.
    Mello, C. B.
    Lepienski, C. M.
    SURFACE & COATINGS TECHNOLOGY, 2010, 204 (18-19): : 3018 - 3021
  • [8] Wear behaviour of Ti6Al4V alloy blasted with zirconia/hydroxyapatite powders
    Yoruc, A. B. Hazar
    Elkoca, O.
    Yildiz, Harika Eksioglu
    Koyun, Ahmet
    INDUSTRIAL LUBRICATION AND TRIBOLOGY, 2014, 66 (01) : 106 - 110
  • [9] Effect of Heat Treatment on Wear Behaviour of Duplex Coatings on Ti6Al4V
    Reddy, K. Raghu Ram Mohan
    Sarcar, M. M. M.
    Ramanaiah, N.
    INTERNATIONAL CONFERENCE ON DESIGN AND MANUFACTURING (ICONDM2013), 2013, 64 : 888 - 895
  • [10] Tribological effects of plasma immersion ion implantation heating treatments on Ti-6Al-4V alloy
    Mello, C. B.
    Ueda, M.
    Silva, M. M.
    Reuther, H.
    Pichon, L.
    Lepienski, C. M.
    WEAR, 2009, 267 (5-8) : 867 - 873
12345