Preparation of high-performance Sb2S3 based visible-light photodetector with excellent reversibility

被引：11
作者：
Aslan, Esra [1 ]
Zarbali, Maharram [1 ]
机构：
[1] Harran Univ, Fac Arts & Sci, Dept Phys, TR-63290 Sanliurfa, Turkey
来源：
OPTICAL MATERIALS | 2022年 / 133卷
关键词：
Antimony sulfide; Photodetector; Sol -gel deposition; OPTICAL-PROPERTIES; SOLAR-CELLS; THIN-FILMS; GEL;
D O I：
10.1016/j.optmat.2022.113028
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In this study, Sb2S3 films were prepared by dip coating method at 250, 300, 350, 400 and 450 degrees C temperatures. No heat treatment was applied other than the coating temperatures. XRD, SEM, EDX and photoluminescence measurements of the prepared films were carried out. In addition, metal-semiconductor-metal (MSM) type photodetectors were prepared using Sb2S3 films. According to XRD and SEM results, films coated at 250 degrees C are still in amorphous structure. On the other hand, the films begin to crystallize at 300 degrees C. The EDX results show that the S/Sb ratio of Sb2S3 films varies between 1.35 and 1.55 depending on the coating temperature. Photoluminescence results show a strong emission peak with an energy value of 1.98 eV for all samples. Photocurrents of the prepared photodetectors vary between 0.44 and 48.15 nA depending on the coating temperature. A photosensitivity of 56.81 was observed with the photodetector prepared at 400 degrees C. In addition, Sb2S3 photodetectors prepared at 400 degrees C exhibit rise and decay times of -0.4 and -0.4 s, respectively with an excellent reversibility.
引用
收藏
页数：10
相关论文
共 38 条
[1]   Tuning of photosensitivity and optical parameters of ZnO based photodetectors by co-Sn and Ti doping [J].
Aslan, Esra ;
Zarbali, Maharram .
OPTICAL MATERIALS, 2022, 125
[2]   Highly sensitive zinc oxide ultraviolet photodetector by titanium incorporation [J].
Aslan, Esra ;
Zarbali, Maharram .
THIN SOLID FILMS, 2021, 724
[3]  
Bras Patrice, 2014, 2014 IEEE 40th Photovoltaic Specialists Conference (PVSC), P0328, DOI 10.1109/PVSC.2014.6924924
[4]   CuInS2/Sb2S3 heterostructure modified with noble metal co-catalyst for efficient photoelectrochemical water splitting [J].
Cai, Qijun ;
Liu, Zhifeng ;
Han, Changcun ;
Tong, Zhengfu ;
Ma, Chonghao .
JOURNAL OF ALLOYS AND COMPOUNDS, 2019, 795 :319-326
[5]   Synthesis of Sb2S3 nanowall arrays for high performance visible light photodetectors [J].
Chao, Junfeng ;
Xing, Shumin ;
Zhang, Jijun ;
Qin, Changhai ;
Duan, Degong ;
Wu, Xinhui ;
Shen, Qingchao .
MATERIALS RESEARCH BULLETIN, 2014, 57 :300-305
[6]   Controlled Synthesis of Ultrathin Sb2Se3 Nanowires and Application for Flexible Photodetectors [J].
Chen, Guihuan ;
Wang, Wenliang ;
Wang, Chunde ;
Ding, Tao ;
Yang, Qing .
ADVANCED SCIENCE, 2015, 2 (10)
[7]   Efficient Sb2S3-Sensitized Solar Cells Via Single-Step Deposition of Sb2S3 Using S/Sb-Ratio-Controlled SbCl3-Thiourea Complex Solution [J].
Choi, Yong Chan ;
Seok, Sang Il .
ADVANCED FUNCTIONAL MATERIALS, 2015, 25 (19) :2892-2898
[8]   A theoretical study on Sb2S3 solar cells: The path to overcome the efficiency barrier of 8% [J].
Courel, Maykel ;
Jimenez, Thalia ;
Arce-Plaza, A. ;
Seuret-Jimenez, D. ;
Moran-Lazaro, J. P. ;
Sanchez-Rodriguez, F. J. .
SOLAR ENERGY MATERIALS AND SOLAR CELLS, 2019, 201
[9]  
Cullity BD., 1978, Elements of X-Ray Diffraction, Vsecond
[10]   Elucidating the role of graphene and porous carbon coating on nanostructured Sb2S3 for superior lithium and sodium storage [J].
Dashairya, Love ;
Das, Debasish ;
Saha, Partha .
JOURNAL OF ALLOYS AND COMPOUNDS, 2021, 883
1234