Magnetic force microscope tips coated with FePd, FePt, and CoPt alloy films

被引：10
|
作者：
Ishihara, Shinji [1 ]
Ohtake, Mitsuru [1 ]
Futamoto, Masaaki [1 ]
机构：
[1] Chuo Univ, Fac Sci & Engn, Bunkyo Ku, Tokyo 1128551, Japan
来源：
THIN SOLID FILMS | 2013年 / 546卷
关键词：
Magnetic force microscope tip; Resolution; Switching field; Ordered alloy; FePd; FePt; CoPt; ELECTRON-BEAM;
D O I：
10.1016/j.tsf.2013.06.052
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Magnetic force microscope (MFM) tips are prepared by coating Si tips of 4 nm radius with FePd, FePt, and CoPt films of 80 nm thickness at room temperature followed by annealing at 600 degrees C. The spatial resolution and the switching field are investigated. The resolution of about 9 nm is realized for all the tips. On the contrary, the switching fields of FePd-, FePt-, and CoPt- coated tips are 117.4, 37.8, and 268.6 kA/m, respectively. The crystal structure and the magnetic properties of coated magnetic thin films prepared on flat Si substrates are measured and the interrelationships with the MFM tip characteristics are briefly investigated. (C) 2013 Elsevier B.V. All rights reserved.
引用
收藏
页码：205 / 210
页数：6
相关论文
共 50 条
  • [31] Preparation of L10 ordered FePd, FePt, and CoPt thin films with flat surfaces on MgO(001) single-crystal substrates
    Itabashi, Akira
    Ohtake, Mitsuru
    Ouchi, Shouhei
    Kirino, Fumiyoshi
    Futamoto, Masaaki
    JEMS 2012 - JOINT EUROPEAN MAGNETIC SYMPOSIA, 2012, 40
  • [32] L10 Ordered FePd, FePt, and CoPt Thin Films With Flat Surfaces Prepared on MgO(110) Single-Crystal Substrates
    Ohtake, Mitsuru
    Itabashi, Akira
    Kirino, Fumiyoshi
    Futamoto, Masaaki
    IEEE TRANSACTIONS ON MAGNETICS, 2013, 49 (07) : 3295 - 3298
  • [33] Effect of Magnetic Film Thickness on the Spatial Resolution of Magnetic Force Microscope Tips
    Nagano, Katsumasa
    Tobari, Kousuke
    Ohtake, Mitsuru
    Futamoto, Masaaki
    JOINT EUROPEAN MAGNETIC SYMPOSIA (JEMS), 2011, 303
  • [34] Magnetic force microscope tip-induced remagnetization of CoPt nanodisks with perpendicular anisotropy
    Mironov, V.L.
    Gribkov, B.A.
    Vdovichev, S.N.
    Gusev, S.A.
    Fraerman, A.A.
    Ermolaeva, O.L.
    Shubin, A.B.
    Alexeev, A.M.
    Zhdan, P.A.
    Binns, C.
    Journal of Applied Physics, 2009, 106 (05):
  • [35] Magnetic force microscope tip-induced remagnetization of CoPt nanodisks with perpendicular anisotropy
    Mironov, V. L.
    Gribkov, B. A.
    Vdovichev, S. N.
    Gusev, S. A.
    Fraerman, A. A.
    Ermolaeva, O. L.
    Shubin, A. B.
    Alexeev, A. M.
    Zhdan, P. A.
    Binns, C.
    JOURNAL OF APPLIED PHYSICS, 2009, 106 (05)
  • [36] Pulsed magnetic field magnetic force microscope and evaluation of magnetic properties of soft magnetic tips
    Zheng, Yangdong
    Yoshimura, Satoru
    Egawa, Genta
    Zheng, Fu
    Kinoshita, Yukinori
    Saito, Hitoshi
    JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2015, 48 (33)
  • [37] Magnetic properties of electron beam evaporated CoPt alloy thin films
    Yamada, Y
    Suzuki, T
    Abarra, EN
    IEEE TRANSACTIONS ON MAGNETICS, 1997, 33 (05) : 3622 - 3624
  • [38] Magnetic properties of electron beam evaporated CoPt alloy thin films
    Yamada, Y
    Suzuki, T
    Abarra, EN
    IEEE TRANSACTIONS ON MAGNETICS, 1998, 34 (02) : 343 - 345
  • [39] Magnetic properties of electron beam evaporated CoPt alloy thin films
    Yamada, Y.
    Suzuki, T.
    Abarra, E.N.
    IEEE Transactions on Magnetics, 1998, 34 (2 pt 1): : 343 - 345
  • [40] Magnetic patterning perpendicular anisotropy FePd alloy films by masked ion irradiation
    Merkel, D. G.
    Bottyan, L.
    Tancziko, F.
    Zolnai, Z.
    Nagy, N.
    Vertesy, G.
    Waizinger, J.
    Bommer, L.
    JOURNAL OF APPLIED PHYSICS, 2011, 109 (12)
12345