Mechanical properties of porous metastable beta Ti-Nb-Zr alloys for biomedical applications

被引:37
作者
Brailovski, V. [1 ]
Prokoshkin, S. [2 ]
Gauthier, M. [3 ]
Inaekyan, K. [1 ]
Dubinskiy, S. [1 ,2 ]
机构
[1] Ecole Technol Super, Montreal, PQ H3C 1K3, Canada
[2] Natl Univ Sci & Technol MISIS, Moscow 119049, Russia
[3] Govt Canada, Natl Res Council, IMI, Boucherville, PQ J4B 6Y4, Canada
基金
加拿大自然科学与工程研究理事会;
关键词
Metals and alloys; Powder metallurgy; Sintering; Mechanical properties; Shape memory; TITANIUM-ALLOY; SHAPE-MEMORY; TRANSFORMATION; NI;
D O I
10.1016/j.jallcom.2011.12.157
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
For this study, Ti-(20-22)Nb-(5-6)Zr (at%) ingots were manufactured by vacuum and argon arc melting. The obtained ingots were divided into two batches: the first subjected to cold rolling (CR) from 30 to 85% of thickness reduction, and subsequent annealing in the 450-600 degrees C temperature range (1 h). Regardless of the CR intensity, Ti-Nb-Zr samples subjected to 600 degrees C annealing showed the highest fatigue resistance during room-temperature cumulative cycling due to the stress-induced martensitic transformation occurring in the polygonized dislocation substructure (average subgrain size similar to 100 nm). The second batch was atomized to produce 100-mu m-size powders in order to manufacture open-cell porous material (cell size vary from 136 to 561 mu m) of 46% porosity by means of powder metallurgy using a polymer-based foaming process. Tensile, compression and bending testing were performed at RT on foam samples annealed at 450-600 degrees C (1 h). Results indicated that Young's modulus of Ti-Nb-Zr foams significantly decreases as compared to the as-sintered material: when annealing temperature increases from 450 to 600 degrees C, Young's modulus decreases from 10 +/- 2 GPa to 6 +/- 1 GPa. Under the same testing conditions, Ti-CP foams produced by the same technology and having similar porosity remain fairly insensible to post-sintering annealing. (C) 2012 V. Brailovski. Published by Elsevier B.V. All rights reserved.
引用
收藏
页码:S413 / S417
页数:5
相关论文
共 14 条
[1]  
Ashby MF, 2000, METAL FOAM DESIGN GU
[2]   Bulk and porous metastable beta Ti-Nb-Zr(Ta) alloys for biomedical applications [J].
Brailovski, V. ;
Prokoshkin, S. ;
Gauthier, M. ;
Inaekyan, K. ;
Dubinskiy, S. ;
Petrzhik, M. ;
Filonov, M. .
MATERIALS SCIENCE & ENGINEERING C-MATERIALS FOR BIOLOGICAL APPLICATIONS, 2011, 31 (03) :643-657
[3]   Mechanical Properties of Thermomechanically-Processed Metastable Beta Ti-Nb-Zr Alloys for Biomedical Applications [J].
Brailovski, Vladimir ;
Prokoshkin, Sergey ;
Inaekyan, Karine ;
Dubinskiy, Sergey ;
Gauthier, Maxime .
THERMEC 2011, PTS 1-4, 2012, 706-709 :455-+
[4]  
Collings E.W., 1984, TITANIUM ALLOYS
[5]   Super-elastic titanium alloy with unstable plastic deformation [J].
Hao, YL ;
Li, SJ ;
Sun, SY ;
Zheng, CY ;
Hu, QM ;
Yang, R .
APPLIED PHYSICS LETTERS, 2005, 87 (09)
[6]   Martensitic transformation, shape memory effect and superelasticity of Ti-Nb binary alloys [J].
Kim, H. Y. ;
Ikehara, Y. ;
Kim, J. I. ;
Hosoda, H. ;
Miyazaki, S. .
ACTA MATERIALIA, 2006, 54 (09) :2419-2429
[7]  
LEFEBVRE LP, 2001, Patent No. 6660224
[8]   Fatigue properties of a metastable β-type titanium alloy with reversible phase transformation [J].
Li, S. J. ;
Cui, T. C. ;
Hao, Y. L. ;
Yang, R. .
ACTA BIOMATERIALIA, 2008, 4 (02) :305-317
[9]  
MISHRA AK, 1993, BETA TITANIUM ALLOYS IN THE 1990S, P61
[10]   Development and characterization of Ni-free Ti-base shape memory and superelastic alloys [J].
Miyazaki, S. ;
Kim, H. Y. ;
Hosoda, H. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 438 :18-24