Phosphorus equilibrium between hot metal and stag

被引：54

作者：

Lee, CM ^{[1
]}

Fruehan, RJ ^{[1
]}

机构：

[1] Carnegie Mellon Univ, Mat Sci & Engn Dept, Pittsburgh, PA 15213 USA

来源：

IRONMAKING & STEELMAKING | 2005年 / 32卷 / 06期

关键词：

smelting; thermodynamics; dephosphorisation;

D O I：

10.1179/174328105X48142

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

In new smelting processes, such as Hlsmelt, significant dephosphorisation occurs. Whereas there have been many studies of the phosphorus reaction in steelmaking, there have been few studies of the phosphorus equilibrium reaction relevant to smelting slags. A study of the phosphorus equilibrium reaction between liquid iron and MgO saturated slag with low basicity and low iron oxide content is reported. The phosphate capacity and phosphorus distribution ratio have been measured as a function of slag composition at 1823 K. Also, the phosphorus distribution ratio between carbon saturated liquid iron and slag at equilibrium has been calculated from experimental data. The phosphorus distribution ratio is in reasonable agreement with the industrial data for Hlsmelt. The results indicate that significant phosphorus renewal can be achieved in smelting processes.

引用

页码：503 / 508

页数：6

共 25 条

[11]

KUNISADA K, 1987, T IRON STEEL I JPN, V27, P263

[12] Thermodynamics of MnO, FeO, and phosphorus in steelmaking slags with high MnO contents [J].

Morales, AT ;

Fruehan, RJ .

METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 1997, 28 (06) :1111-1118

[13]

RYU JY, 1999, IRON STEELMAKER JAN, P59

[14]

SUITO H, 1984, T IRON STEEL I JPN, V24, P40

[15]

SUITO H, 1981, T IRON STEEL I JPN, V21, P250

[16]

SUITO H, 1982, T IRON STEEL I JPN, V22, P869

[17] THERMODYNAMIC ASSESSMENT OF HOT METAL AND STEEL DEPHOSPHORIZATION WITH MNO-CONTAINING BOF SLAGS [J].

SUITO, H ;

INOUE, R .

ISIJ INTERNATIONAL, 1995, 35 (03) :258-265

[18]

SUITO H, 1984, T IRON STEEL I JPN, V24, P47

[19]

Turkdogan E., 1996, FUNDAMENTALS STEELMA

[20]

Turkdogan E.T., 1980, PHYS CHEM HIGH TEMPE, P81

← 1 2 3 →