Rheological phase synthesis and electrochemical performance of Co3O4 for supercapacitors

被引：1

作者：

Zhao, J. C. ^{[1
]}

Gu, Y. J. ^{[1
]}

Lou, J. ^{[1
]}

Tang, B. H. J. ^{[1
]}

Zheng, J. ^{[1
]}

Xu, J. L. ^{[1
]}

机构：

[1] Shanghai Univ Engn Sci, Coll Chem & Chem Engn, Shanghai, Peoples R China

来源：

RUSSIAN JOURNAL OF ELECTROCHEMISTRY | 2013年 / 49卷 / 11期

关键词：

supercapacitor; Co3O4; rheological phase reaction; electrochemical performance; CAPACITANCE;

D O I：

10.1134/S1023193513110141

中图分类号：

O646 [电化学、电解、磁化学];

学科分类号：

081704 ;

摘要：

Co3O4 was prepared by rheological phase reaction, and the effect of pyrolyzing temperature on the electrochemical performance of Co3O4 was investigated. XRD shows that higher temperature treatment results in sharper diffraction peaks, indicating an increase of particle size of Co3O4. The result of TEM shows that the particle sizes of Co3O4 are about 200 nm. The optimum pyrolyzing temperature is confirmed to be 600A degrees C, and Co3O4 prepared at this temperature exhibits 390.8 F g(-1) of specific capacitance in 6 M KOH electrolyte at the scan rate of 5 mV s(-1). Co3O4 prepared at the temperature of 600A degrees C shows an excellent cyclability.

引用

页码：1053 / 1056

页数：4

共 14 条

[1] Preparation and properties of Co3O4 nanorods as supercapacitor material [J].

Cui, Li ;

Li, Juan ;

Zhang, Xiao-Gang .

JOURNAL OF APPLIED ELECTROCHEMISTRY, 2009, 39 (10) :1871-1876

[2] Carbon materials for the electrochemical storage of energy in capacitors [J].

Frackowiak, E ;

Béguin, F .

CARBON, 2001, 39 (06) :937-950

[3] Electrochemical capacitance of Co3O4 nanowire arrays supported on nickel foam [J].

Gao, Yinyi ;

Chen, Shuli ;

Cao, Dianxue ;

Wang, Guiling ;

Yin, Jinling .

JOURNAL OF POWER SOURCES, 2010, 195 (06) :1757-1760

[4] Principles and applications of electrochemical capacitors [J].

Kötz, R ;

Carlen, M .

ELECTROCHIMICA ACTA, 2000, 45 (15-16) :2483-2498

[5] Characterization of sol-gel-derived cobalt oxide xerogels as electrochemical capacitors [J].

Lin, C ;

Ritter, JA ;

Popov, BN .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1998, 145 (12) :4097-4103

[6] Facile synthesis of Co3O4 nanoflowers grown on Ni foam with superior electrochemical performance [J].

Qing, Xiaoxia ;

Liu, Suqin ;

Huang, Kelong ;

Lv, Kezhen ;

Yang, Youping ;

Lu, Zhouguang ;

Fang, Dong ;

Liang, Xinxing .

ELECTROCHIMICA ACTA, 2011, 56 (14) :4985-4991

[7] Capacitance studies of cobalt oxide films formed via electrochemical precipitation [J].

Srinivasan, V ;

Weidner, JW .

JOURNAL OF POWER SOURCES, 2002, 108 (1-2) :15-20

[8] Carbon electrodes with high pseudocapacitance for supercapacitors [J].

Vol'fkovich, Yu. M. ;

Mikhalin, A. A. ;

Bograchev, D. A. ;

Sosenkin, V. E. .

RUSSIAN JOURNAL OF ELECTROCHEMISTRY, 2012, 48 (04) :424-433

[9] Preparation and electrochemical properties of mesoporous Co3O4 crater-like microspheres as supercapacitor electrode materials [J].

Wang, Lu ;

Liu, Xiaoheng ;

Wang, Xin ;

Yang, Xujie ;

Lu, Lude .

CURRENT APPLIED PHYSICS, 2010, 10 (06) :1422-1426

[10] Pseudocapacitive properties of electrodeposited porous nanowall Co3O4 film [J].

Wu, J. B. ;

Lin, Y. ;

Xia, X. H. ;

Xu, J. Y. ;

Shi, Q. Y. .

ELECTROCHIMICA ACTA, 2011, 56 (20) :7163-7170

← 1 2 →