Calcium sulfoaluminate clinker hydration at different alkali concentrations

被引：53

作者：

Padilla-Encinas, P. ^{[1
]}

Palomo, A. ^{[1
]}

Blanco-Varela, M. T. ^{[1
]}

Fernandez-Jimenez, A. ^{[1
]}

机构：

[1] Eduardo Torroja Inst Construct Sci IETcc CSIC, Madrid, Spain

来源：

CEMENT AND CONCRETE RESEARCH | 2020年 / 138卷

关键词：

Calcium sulfoaluminate clinker; NaOH concentration; Al-27; MAS-NMR; AL-27 MAS NMR; C-S-H; PORTLAND CEMENTS; ALUMINUM; PHASE; EXPANSION; PRODUCTS; FIELD;

D O I：

10.1016/j.cemconres.2020.106251

中图分类号：

TU [建筑科学];

学科分类号：

0813 ;

摘要：

This paper discusses the effect of alkalis on strength development and hydration products in a commercial calcium sulfoaluminate clinker (KCSA). KCSA pastes were hydrated with water and 0.1 M, 1 M, 2 M, 4 M and 8 M NaOH. The hydration products were characterised at 3d, 28d and 90d, by XRD, SEM, DTA/TG and Al-27 MAS-NMR. With 0.1 M, 1 M and 2 M, the main hydration products were similar to those observed in the water-hydrated pastes: ettringite, AH(3) and calcium aluminate hydrates such as CAH(10); Al-27 MAS-NMR analysis revealed different degrees of crystallinity in AH(3). With 4 M and 8 M, ettringite was not detected, AH(3) crystallinity rose and siliceous hydrogarnet, calcium carboaluminate hydrates, thenardite and calcite were formed at higher alkalinity. Sample carbonation, which grew more intense with time and at higher alkalinity, yielded calcium carbonate and an aluminium hydroxide gel inducing cracking.

引用

页数：12

共 43 条

[21] A STUDY ON THE HYDRATION PRODUCTS OF A NON-EXPANSIVE SULFOALUMINATE CEMENT [J].

KASSELOURI, V ;

TSAKIRIDIS, P ;

MALAMI, C ;

GEORGALI, B ;

ALEXANDRIDOU, C .

CEMENT AND CONCRETE RESEARCH, 1995, 25 (08) :1726-1736

[22] Use of fly ash and phosphogypsum for the synthesis of belite-sulfoaluminate clinker [J].

Kramar, S. ;

Zibret, L. ;

Fidanchevska, E. ;

Jovanov, V. ;

Angjusheva, B. ;

Ducman, V. .

MATERIALES DE CONSTRUCCION, 2019, 69 (333)

[23]

Lan W., 1996, ADV CEM RES, V8, P127, DOI [10.1680/adcr.2002.14.4.141, DOI 10.1680/ADCR.1996.8.31.127]

[24] Lime as an Anti-Plasticizer for Self-Compacting Clay Concrete [J].

Landrou, Gnanli ;

Brumaud, Coralie ;

Winnefeld, Frank ;

Flatt, Robert J. ;

Habert, Guillaume .

MATERIALS, 2016, 9 (05)

[25] Hydration of Portland cement with additions of calcium sulfoaluminates [J].

Le Saout, Gwenn ;

Lothenbach, Barbara ;

Hori, Aldhiro ;

Higuchi, Takayuki ;

Winnefeld, Frank .

CEMENT AND CONCRETE RESEARCH, 2013, 43 :81-94

[26] The AFm phase in Portland cement [J].

Matschei, T. ;

Lothenbach, B. ;

Glasser, F. P. .

CEMENT AND CONCRETE RESEARCH, 2007, 37 (02) :118-130

[27] Effect of temperature and aluminium on calcium (alumino)silicate hydrate chemistry under equilibrium conditions [J].

Myers, Rupert J. ;

L'Hopital, Emilie ;

Provis, John L. ;

Lothenbach, Barbara .

CEMENT AND CONCRETE RESEARCH, 2015, 68 :83-93

[28] C4A3S HYDRATION, ETTRINGITE FORMATION, AND ITS EXPANSION MECHANISM .3. EFFECT OF CAO, NAOH AND NACL - CONCLUSIONS [J].

OGAWA, K ;

ROY, DM .

CEMENT AND CONCRETE RESEARCH, 1982, 12 (02) :247-256

[29]

Ost BWA, 1975, US Patent, Patent No. 3860433

[30] A review on alkaline activation: new analytical perspectives [J].

Palomo, A. ;

Krivenko, P. ;

Garcia-Lodeiro, I. ;

Kavalerova, E. ;

Maltseva, O. ;

Fernandez-Jimeneza, A. .

MATERIALES DE CONSTRUCCION, 2014, 64 (315)

← 1 2 3 4 5 →