Effect of Additive Cu-10Sn on Sintering Behavior and Wear Resistance of 316L Stainless Steel

被引：9
作者：
Yang Xia [1 ]
Bai Ying-long [1 ]
Xu Meng [1 ]
Guo Shi-ju [1 ]
机构：
[1] Univ Sci & Technol Beijing, Inst Adv Mat & Technol, Beijing 100083, Peoples R China
来源：
JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL | 2013年 / 20卷 / 07期
关键词：
stainless steel; powder metallurgy; wear resistance; sliding wear; sintering behavior; HIGH-SPEED STEEL; MECHANICAL-PROPERTIES; MICROSTRUCTURE; CORROSION; COPPER; H2SO4;
D O I：
10.1016/S1006-706X(13)60131-4
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Austenitic 316L stainless steel has good corrosion resistance; however, the relative softness often limits its application. Severe adhesive wear often occurs between the 316L stainless steel and the metal counterpart. Cu-10Sn alloy is often used to improve the wear resistance of powder metallurgy 316L stainless steel. The influence of Cu-10Sn on sintering behavior and wear resistance of powder metallurgy 316L stainless steel was investigated. The parameters investigated included sintering temperature and volume percent of Cu-10Sn. A maximum relative density of 97% was achieved with 25% (in volume percent) Cu-10Sn content at a sintering temperature of 1 300 degrees C for 60 mm. The irregular and sharp angles of 316L stainless steel particles become round, and the pores are removed completely as a result of large amount of liquid phase formed during sintering. The minimum friction mass loss was achieved with 25% Cu-10Sn content.
引用
收藏
页码：84 / 88
页数：5
相关论文
共 50 条
[31]   Effect of Initial Surface Scratches on the Cavitation Erosion Behavior of 316L Stainless Steel Substrates and 316L Stainless Steel Coatings [J].
Lu, Pengfei ;
Xu, Ziqi ;
Tian, Ye ;
Yang, Rui ;
Hu, Kaixin ;
Li, Hua ;
Yin, Yanhong ;
Chen, Xiuyong .
MATERIALS, 2023, 16 (04)
[32]   An investigation of the corrosion behavior of 316L stainless steel fabricated by SLM and SPS techniques [J].
Kale, Amol B. ;
Kim, Byung-Kyu ;
Kim, Dong-Ik ;
Castle, E. G. ;
Reece, M. ;
Choi, Shi-Hoon .
MATERIALS CHARACTERIZATION, 2020, 163
[33]   The wear and corrosion resistance of shot peened-nitrided 316L austenitic stainless steel [J].
Hashemi, B. ;
Yazdi, M. Rezaee ;
Azar, V. .
MATERIALS & DESIGN, 2011, 32 (06) :3287-3292
[34]   Microstructure and Wear Resistance of Carbon Fibers Reinforced 316L Stainless Steel Prepared Using Laser Cladding [J].
He Songya ;
Liu Xiaodong ;
Zhao Shuzhen ;
Jin Jianbo ;
Zhou Shengfeng .
CHINESE JOURNAL OF LASERS-ZHONGGUO JIGUANG, 2020, 47 (05)
[35]   Anisotropic Wear Resistance of Heat-Treated Selective Laser-Melted 316L Stainless Steel [J].
Sun, Menghui ;
Zhang, Qianqian ;
Wu, Jinxiu ;
Wang, Hao ;
Wang, Xu ;
Zhang, Hao ;
An, Yinong ;
Liu, Yujie ;
Ma, Long .
LUBRICANTS, 2025, 13 (04)
[36]   Comparison of Different Additive Manufacturing Methods for 316L Stainless Steel [J].
Bedmar, Javier ;
Riquelme, Ainhoa ;
Rodrigo, Pilar ;
Torres, Belen ;
Rams, Joaquin .
MATERIALS, 2021, 14 (21)
[37]   Corrosion and wear behaviors of boronized AISI 316L stainless steel [J].
Kayali, Yusuf ;
Buyuksagis, Aysel ;
Yalcin, Yllmaz .
METALS AND MATERIALS INTERNATIONAL, 2013, 19 (05) :1053-1061
[38]   Study on Debinding and Sintering Conditions in Extrusion-Based Additive Manufacturing of 316L and 316L+Cu [J].
Silvain, Jean-Francois ;
Gifford, Daniel Lincoln ;
Fourcade, Sebastien ;
Cuzacq, Laurent ;
Grosseau-Poussard, Jean-Luc ;
Debiemme-Chouvy, Catherine ;
Doyen, Nicolas Tessier ;
Lu, Yongfeng .
METALS, 2023, 13 (11)
[39]   Twinning induced plasticity in austenitic stainless steel 316L made by additive manufacturing [J].
Pham, M. S. ;
Dovgyy, B. ;
Hooper, P. A. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2017, 704 :102-111
[40]   High temperature stability of laser additive manufactured stainless steel 316L structures [J].
Hou, J. ;
Iqbal, N. ;
Jimenez-Melero, E. .
MATERIALS TODAY COMMUNICATIONS, 2025, 46
12345