Effect of Additive Cu-10Sn on Sintering Behavior and Wear Resistance of 316L Stainless Steel

被引：9

作者：

Yang Xia ^{[1
]}

Bai Ying-long ^{[1
]}

Xu Meng ^{[1
]}

Guo Shi-ju ^{[1
]}

机构：

[1] Univ Sci & Technol Beijing, Inst Adv Mat & Technol, Beijing 100083, Peoples R China

来源：

JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL | 2013年 / 20卷 / 07期

关键词：

stainless steel; powder metallurgy; wear resistance; sliding wear; sintering behavior; HIGH-SPEED STEEL; MECHANICAL-PROPERTIES; MICROSTRUCTURE; CORROSION; COPPER; H2SO4;

D O I：

10.1016/S1006-706X(13)60131-4

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Austenitic 316L stainless steel has good corrosion resistance; however, the relative softness often limits its application. Severe adhesive wear often occurs between the 316L stainless steel and the metal counterpart. Cu-10Sn alloy is often used to improve the wear resistance of powder metallurgy 316L stainless steel. The influence of Cu-10Sn on sintering behavior and wear resistance of powder metallurgy 316L stainless steel was investigated. The parameters investigated included sintering temperature and volume percent of Cu-10Sn. A maximum relative density of 97% was achieved with 25% (in volume percent) Cu-10Sn content at a sintering temperature of 1 300 degrees C for 60 mm. The irregular and sharp angles of 316L stainless steel particles become round, and the pores are removed completely as a result of large amount of liquid phase formed during sintering. The minimum friction mass loss was achieved with 25% Cu-10Sn content.

引用

页码：84 / 88

页数：5

共 50 条

[1] Effect of Additive Cu-10Sn on Sintering Behavior and Wear Resistance of 316L Stainless Steel [J].

Xia Yang ;

Ying-long Bai ;

Meng Xu ;

Shi-ju Guo .

Journal of Iron and Steel Research International, 2013, 20 :84-88

[2] Effect of Additive Cu-10Sn on Sintering Behavior and Wear Resistance of 316L Stainless Steel [J].

YANG Xia ;

BAI Ying-long ;

XU Meng ;

GUO Shi-ju .

JournalofIronandSteelResearch(International), 2013, 20 (07) :84-88

[3] Preparation and properties of Cu-10Sn alloy infiltrated 316L stainless steel composites [J].

Yang, Xia ;

Bai, Yinglong ;

Xu, Meng ;

Guo, Shiju .

FRONTIERS OF MANUFACTURING SCIENCE AND MEASURING TECHNOLOGY II, PTS 1 AND 2, 2012, 503-504 :552-555

[4] Reciprocating sliding wear of the sintered 316L stainless steel with boron additions [J].

Peruzzo, M. ;

Serafini, F. L. ;

Ordonez, M. F. C. ;

Souza, R. M. ;

Farias, M. C. M. .

WEAR, 2019, 422 :108-118

[5] Microstructure effect on sliding wear of 316L stainless steel selectively laser melted [J].

Barrionuevo, German Omar ;

Walczak, Magdalena ;

Ramos-Grez, Jorge ;

Mendez, Patricio ;

Debut, Alexis .

MATERIALS SCIENCE AND TECHNOLOGY, 2024, 40 (06) :466-478

[6] Effect of Strain Hardening on Wear and Corrosion Resistance of 316L Austenitic Stainless Steel [J].

Huang, Jiaqi ;

Sun, Guoqing ;

Peng, Jian ;

Wu, Wangping .

JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2024, 33 (16) :8108-8121

[7] Hardness and wear resistance of roller burnished 316L stainless steel [J].

Tugay, Ibrahim Orhun ;

Hosseinzadeh, Ali ;

Yapici, Guney Guven .

MATERIALS TODAY-PROCEEDINGS, 2021, 47 :2405-2409

[8] Annealing Effect on Wear Resistance of Nanostructured 316L Stainless Steel Subjected to Dynamic Plastic Deformation [J].

Wang, Bo ;

Yao, Bin ;

Han, Zhong .

JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2012, 28 (10) :871-877

[9] Effect of Microstructural Anisotropy on Corrosion Resistance of 316L Stainless Steel Prepared by Additive Manufacturing [J].

Zheng Zhijun ;

Mao Lingyan ;

Dong Zhihao .

CHINESE JOURNAL OF LASERS-ZHONGGUO JIGUANG, 2023, 50 (04)

[10] Improvement of the wear resistance of 316L stainless steel by laser surface alloying [J].

Tassin, C ;

Laroudie, F ;

Pons, M ;

Lelait, L .

SURFACE & COATINGS TECHNOLOGY, 1996, 80 (1-2) :207-210

← 1 2 3 4 5 →